Method of manufacturing artificial marble
A method for the preparation of an engineered stone slab having coated lumps of composite stone material, the method comprising: scooping a first inorganic particulate material and a polymer material to produce lumps of composite stone material; mixing a second inorganic particulate material with the lumps to produce coated lumps; and adding one or more colorants to the first inorganic particulate material, to the second inorganic particulate material, or to both the first and second inorganic particulate materials.
1. A method for the preparation of an engineered stone slab having coated lumps of composite stone material, the method comprising:
scooping a first inorganic particulate material and a polymer material to produce lumps of composite stone material;
mixing a second inorganic particulate material with the lumps to produce coated lumps; and
adding one or more colorants to the first inorganic particulate material, to the second inorganic particulate material, or to both the first and second inorganic particulate materials.
2. The method of claim 1 , wherein said scooping, the mixing or both are performed in a mixer having a mixing hook which comprises an extension.
3. The method of claim 2 wherein said extension comprises a flat surface, two interconnected surfaces, a spoon-shaped surface or any combination thereof.
4. The method of claim 1 , wherein the first inorganic particulate material, the second inorganic particulate material, or both, comprise quartz.
5. The method of claim 1 , wherein the coated lumps comprise an inner core having a first property and an outer layer having a second property.
6. The method of claim 5 , wherein the property comprises color, texture, density, chemical composition, hardness, porousivity or any combination thereof.
7. The method of claim 1 , wherein the first inorganic particulate material comprises particles having a size range of about 0.05 mm to about 5 mm.
8. The method of claim 1 , wherein the second inorganic particulate material comprises particles having a size range of about 35 micron to about 50 microns.
9. The method of claim 1 , wherein polymer comprises a binder, hardener, initiator, or any combination thereof.
10. The method of claim 1 , wherein the shape of the lumps is substantially round, substantially circular, spiked, or any combination thereof.
11. The method of claim 1 , wherein the scooping is performed at a varying mixing speed.
12. The method of claim 1 , wherein the mixing is performed at a varying mixing speed.
13. The method of claim 1 , further comprising mixing a third inorganic particulate material with the coated lumps to produce multi-layer coated lumps.