Method of producing silica sols with controllable broad size distribution and minimum particle size
View Patent ↗Colloidal silica having a controllable broad particle size distribution and a controllable minimum particle size is disclosed and claimed. Particles below a predetermined size are excluded from the product colloidal silica of the invention. A method for continuously producing the desired colloidal composition is disclosed comprising the steps of providing preformed silica particles having a surface area which controls the particle size of the colloidal silica product, adding a feed silica comprising an alkaline solution and silicate at a feed rate which is less than a nucleation rate.
1. A method for producing colloidal silica particles having a broad particle size distribution, the method comprising, in any order:
(a) feeding a first component including preformed silica sol particles of predetermined minimum particle size to at least one agitated, heated reactor;
(b) adding a second component including silicic acid to said reactor, wherein the second component is fed to the reactor at a rate that is less than a new silica particle nucleation rate;
(c) adding a third component including an alkaline agent to the reactor; and
(d) wherein the minimum particle size of the resulting colloidal silica is controlled by the particle size of the first component, and wherein the broad particle size distribution is dependent on the ratio of the feed rates of the first component to the second component.
2. The method of claim 1 , wherein essentially all of the produced colloidal silica particles are larger than the preformed silica sol particles of the first component.
3. The method of claim 1 , wherein an average particle size of the broad particle size distribution is determined by an average particle size of the first component.
4. The method of claim 1 , wherein an average particle size of the broad particle size distribution is determined by the ratio of the feed rates of the first component to the second component.
5. The method of claim 4 , wherein increasing said ratio causes the broad particle size distribution curve to become wider.
6. The method of claim 4 , including causing an average particle size of the broad particle size distribution curve to increase.
7. The method of claim 1 , including creating a narrower particle size distribution curve without changing an average produced particle size by including in the first component larger preformed silica sol particles and increasing a second component to first component feed rate ratio.
8. The method of claim 1 , wherein said reactor is a single overflow reactor.
9. The method of claim 1 , wherein said reactor is a series of reactors.
10. The method of claim 1 , including concentrating the produced colloidal silica particles.
11. The method of claim 1 , including concentrating via evaporation during the reaction.
12. The method of claim 1 , wherein said reactor is maintained at a temperature in the range of about 40 to about 200° C.
13. The method of claim 1 , wherein the alkaline agent maintains a pH from about 8.0 to about 12.5.
14. The method of claim 1 , wherein said reactor is held at a constant volume by continuous removal of the produced colloidal silica from the reactor.
15. The method of claim 1 , including operating the method as a continuous process.
16. The method of claim 1 , including maintaining steady-state conditions in said reactor by seeding the reactor with produced colloidal silica particles from a previous run of the reactor.