Process for producing stainless steel pipe
View Patent ↗A process for stainless-steel pipe production which comprises piercing rolling a raw material stainless steel containing, by mass, Cr: 10-30%, to give a hollow shell, elongating rolling the hollow shell using a mandrel bar, together with a graphite-free lubricant, to give a finishing rolling blank pipe and heating the blank pipe in a reheating furnace and subjecting the same to finishing rolling by sizing rolling to produce a hot-finished pipe, and then subjecting this pipe as a mother pipe to cold working to produce a stainless-steel pipe. In the reheating furnace, the finishing rolling blank pipe is heated to 1000° C. or more and subjected to heating in which an oxidizing gas is blown into the pipe inside, whereby a stainless-steel pipe which is inhibited from forming a carburized layer in the pipe inner surface can be produced. When the finishing rolling by sizing rolling to give a cold working mother pipe is carried out by stretch reducer rolling at 860-1050° C., an annealing heat treatment of the mother pipe for cold working can be omitted. Thus, a stainless-steel pipe having excellent surface quality can be efficiently produced.
1. A process for producing stainless steel pipes by subjecting a stainless steel raw material containing, by mass, Cr: 10-30%, to piercing rolling to give a hollow shell, subjecting the hollow shell to elongating rolling to give a finishing rolling blank pipe using a mandrel bar, together with a graphite-free lubricant, and heating the blank pipe in a reheating furnace and subjecting the heated blank pipe to finishing rolling by sizing rolling, wherein
the finishing rolling blank pipe is subjected to heating in which it is heated to a temperature not less than 1000° C. in the reheating furnace and an oxidizing gas is blown into the inside of the finishing rolling blank pipe from one end thereof using a blowing nozzle such that combustion of C is fully promoted in the carburized layer in the inside of the finishing rolling blank pipe.
2. A process for producing stainless steel pipes according to claim 1 , wherein air is the oxidizing gas blown into the inside of the finishing rolling blank pipe from one end thereof using a blowing nozzle in the reheating furnace and wherein the air flow rate R (liters/second) and the air blowing time t (seconds) of the air blown into the inside of the finishing rolling blank pipe satisfy the conditions specified by the following formula (1):
240 ≦R×t≦ 2100 (1)
wherein combustion of C is fully promoted in the carburized layer in the inside of the finishing rolling blank pipe.
3. A process for producing stainless steel pipes by subjecting a stainless steel raw material containing, by mass, Cr: 10-30%, to piercing rolling to give a hollow shell, subjecting the hollow shell to elongating rolling to give a finishing rolling blank pipe using a mandrel bar, together with a graphite-free lubricant, and heating the blank pipe in a reheating furnace and subjecting the heated blank pipe to finishing rolling to give a mother pipe by sizing rolling and subjecting the mother pipe to cold working, wherein
the finishing rolling blank pipe is subjected to heating in which it is heated to a temperature not less than 1000° C. in the reheating furnace and an oxidizing gas is blown into the inside of the finishing rolling blank pipe from one end thereof using a blowing nozzle such that combustion of C is fully promoted in the carburized layer in the inside of the finishing rolling blank pipe.
4. A process for producing stainless steel pipes according to claim 3 , wherein air is the oxidizing gas blown into the inside of the finishing rolling blank pipe from one end thereof using a blowing nozzle in the reheating furnace and wherein the air flow rate R (liters/second) and the air blowing time t (seconds) of the air blown into the inside of the finishing rolling blank pipe satisfy the conditions specified by the following formula (1):
240 ≦R×t≦ 2100 (1)
wherein combustion of C is fully promoted in the carburized layer in the inside of the finishing rolling blank pipe.