NITRIDE-BASED RED PHOSPHORS
Embodiments of the present invention are directed to the fluorescence of a nitride-based deep red phosphor having at least one of the following novel features: 1) an oxygen content less than about 2 percent by weight, and 2) a halogen content. Such phosphors are particularly useful in the white light illumination industry, which utilizes the so-called “white LED.” The selection and use of a rare earth halide as a raw material source of not only the activator for the phosphor, but also the halogen, is a key feature of the present embodiments. The present phosphors have the general formula M a M b B C (N,D):Eu 2+ , where M a is a divalent alkaline earth metal such as Mg, Ca, Sr, Ba; M b is a trivalent metal such as Al, Ga, Bi, Y, La, and Sm; and M c is a tetravalent element such as Si, Ge, P, and B; N is nitrogen, and D is a halogen such as F, Cl, or Br. An exemplary compound is CaAlSi(N 1-x F x ): Eu 2+ .
1 . A nitride-based red phosphor having the formula M-A-B—(N,D):Z, wherein:
M is a divalent element;
A is a trivalent element
B is a tetravalent element
N is nitrogen
Z is an activator; and
D is a halogen;
wherein the phosphor is configured to emit visible light having a peak emission wavelength greater than about 620 nm.
2 . The nitride-based red phosphor of claim 1 , wherein the oxygen content is less than about 2 percent by weight.
3 . A nitride-based red phosphor having the formula M m M a M b (N,D) n :Z z , wherein:
M m is a divalent element;
M a is a trivalent element
M b is a tetravalent element
N is nitrogen
Z is an activator; and
D is a halogen;
wherein the stiochiometry of the constituent elements (m+z):a:b:n is about 1:1:1:3, and the phosphor is configured to emit visible light having a peak emission wavelength greater than about 620 nm.
4 . The nitride-based red phosphor of claim 3 , wherein the oxygen content is less than about 2 percent by weight.
5 . A nitride-based red phosphor having the formula M m M a M b D 3w N [(2/3)m+z+a+(4/3)b-w] Z z , wherein:
M m is a divalent element selected from the group consisting of Be, Mg, Ca, Sr, Ba, Zn, Cd, and Hg;
M a is a trivalent element selected from the group consisting of B, Al, Ga, In, Y, Sc, P, As, La, Sm, Sb, and Bi;
M b is a tetravalent element selected from the group consisting of C, Si, Ge, Sn, Ni, Hf, Mo, W, Cr, Pb, Ti, and Zr;
D is a halogen selected from the group consisting of F, Cl, Br, and I;
Z is an activator selected from the group consisting of Eu, Ce, Mn, Tb, and Sm;
N is nitrogen; where
0.01≦m≦1.5;
0.01≦a≦1.5;
0.01≦b≦1.5;
0.0001≦w≦0.6, and
0.0001≦z≦0.5;
wherein the phosphor is configured to emit visible light having a peak emission wavelength greater than about 620 nm.
6 . The nitride-based red phosphor of claim 5 , wherein the oxygen content is less than about 2 percent by weight.
7 . A nitride-based red phosphor having the formula M-A-B—N:Z, wherein:
M is a divalent element;
A is a trivalent element;
B is a tetravalent element;
N is nitrogen;
Z is an activator; and
D is a halogen;
wherein the phosphor is configured to emit visible light having a peak emission wavelength greater than about 620 nm, and wherein the oxygen content is less than about 2 percent by weight.
8 . A nitride-based red phosphor having the formula M m M a M b N n :Z z , wherein:
M m is a divalent element;
M a is a trivalent element;
M b is a tetravalent element;
N is nitrogen
Z is an activator; and
D is a halogen;
wherein the stiochiometry of the constituent elements (m+z):a:b:n is about 1:1:1:3, and the phosphor is configured to emit visible light having a peak emission wavelength greater than about 620 nm, and wherein the oxygen content is less than about 2 percent by weight.
9 . A nitride-based red phosphor having the formula M m M a M b D 3w N [(2/3)m+z+a+(4/3)b-w ]Z z , wherein:
M m is a divalent element selected from the group consisting of Be, Mg, Ca, Sr, Ba, Zn, Cd, and Hg;
M a is a trivalent element selected from the group consisting of B, Al, Ga, In, Y, Sc, P, As, La, Sm, Sb, and Bi;
M b is a tetravalent element selected from the group consisting of C, Si, Ge, Sn, Ni, Hf, Mo, W, Cr, Pb, Ti, and Zr;
D is a halogen selected from the group consisting of F, Cl, Br, and I;
Z is an activator selected from the group consisting of Eu, Ce, Mn, Tb, and Sm;
N is nitrogen; where
0.01≦m≦1.5;
0.01≦a≦1.5;
0.01≦b≦1.5;
0.0001≦w≦0.6, and
0.0001≦z≦0.5;
wherein the phosphor is configured to emit visible light having a peak emission wavelength greater than about 620 nm.
10 . The nitride-based red phosphor of claim 9 , wherein the oxygen content is less than about 2 percent by weight.