View Patent ↗The present invention relates to proppants which can be used to prop open subterranean formation fractions. Proppant formulations are further disclosed which use one or more proppants of the present invention. Methods to prop open subterranean formation fractions are further disclosed. In addition, other uses for the proppants of the present invention are further disclosed, as well as methods of making the proppants.
1. A proppant comprising a template material and a shell material on said template material, wherein said shell material is reacted with said template material to form a mixed phase of template material and shell material or to form a new phase material different from said template material and shell material, and wherein said proppant has an overall diameter of from about 90 microns to about 1,600 microns, and wherein said proppant has a crush strength of 3,000 psi or greater, wherein said template material consists essentially of ceramic material and said shell material consists essentially of ceramic material.
2. The proppant of claim 1 , wherein said proppant comprises a ceramic material or oxide thereof or a metal oxide with a surface material that comprises nanoparticles that are sintered.
3. The proppant of claim 1 , wherein said proppant is hollow, porous, or a closed foam network.
4. The proppant of claim 2 , wherein said nanoparticles have a primary particle size of from 0.1 nm up to 150 nm.
5. The proppant of claim 2 , wherein said nanoparticles comprise agglomerates alone, or a combination of primary particles and agglomerates.
6. The proppant of claim 2 , wherein said nanoparticles have a combination of primary particles and agglomerates, and wherein said nanoparticles have an average primary particle size of from about 1 nm to about 150 nm and the agglomerates have an average particle size of from about 10 nm to about 350 nm.
7. The proppant of claim 2 , wherein said nanoparticles have a combination of primary particles and agglomerates, and wherein said nanoparticles have a weight ratio of primary particles to agglomerates of from 1:9 to 9:1.
8. The proppant of claim 1 , wherein said proppant has a specific gravity of from 0.6 g/cc to about 2.5 g/cc, and said proppant is spherical and has a sphericity of at least about 0.9.
9. The proppant of claim 1 , wherein said proppant comprises a hollow cenosphere.
10. The proppant of claim 1 , wherein said proppant comprises an aluminate.
11. The proppant of claim 1 , wherein said crush strength is from 5,000 psi to 10,000 psi.
12. The proppant of claim 2 , wherein said surface material has an average grain size of 0.1 micron to 0.5 micron.
13. The proppant of claim 2 , wherein said surface material has a maximum grain size of 1 micron.
14. A proppant formulation comprising the proppant of claim 1 and a carrier.
15. The proppant formulation of claim 14 , wherein said carrier is water or brine.
16. The proppant of claim 1 , wherein said proppant is hollow.
17. The proppant of claim 1 , wherein said proppant is porous.
18. The proppant of claim 1 , wherein said shell material is continuous.
19. The proppant of claim 1 , wherein said shell material is substantially uniform in thickness around the entire outer surface of said template material.
20. The proppant of claim 1 , wherein said shell material has a glassy phase and a crystalline phase.
21. The proppant of claim 1 , wherein said shell material has a glassy phase and a crystalline phase and said template material comprises a ceramic material.
22. The proppant of claim 1 , wherein said shell material has a glassy phase and a crystalline phase and said template material comprises a ceramic cenosphere.
23. The proppant of claim 1 , wherein said template material comprises silica, and said shell material comprises alumina, wherein said mixed phase forms at an interface of said template material and said shell material.
24. The proppant of claim 23 , wherein said mixed phase comprises mullite.