Method of making an article
View Patent ↗A method of making an article having at least one re-entrance surface includes the steps of (a) forming a layer of metal powder on a base, (b) selectively laser fusing portions of the layer, and (c) repeating steps (a) and (b) to form the article, each step (a) being performed on the preceding layer characterised in that prior to performing step (a) in a layer which will initiate the formation of a re-entrant feature reversibly bonding at least some of the unfused underlying powder such that it is stable under the application of the laser.
1. A method of making an article, comprising:
(a) forming a preceding layer of metal powder on a base;
(b) exposing a selected portion of said preceding layer to the energy of a laser to thereby fuse one portion of the layer of metal powder and leave another portion of metal powder in the layer un-fused;
(c) subsequently reversibly bonding a bulk of un-fused metal powder of said preceding layer including at an exposed surface of the preceding layer;
(d) forming a subsequent layer of metal powder on the preceding layer after the un-fused metal powder has been reversibly bonded in the preceding layer; and
(e) exposing the subsequent layer of metal powder, which is located over said exposed surface of the preceding layer, to the energy of a laser to thereby form a re-entrant surface of fused metal powder, wherein the re-entrant surface has an interface with the bulk of reversibly bonded but un-fused metal powder of the preceding layer, and the reversible bonding prevents said bulk of metal powder of the preceding layer from balling up when the metal powder of the subsequent layer is being fused by the energy of the laser.
2. A method as claimed in claim 1 wherein the bonding of said bulk of the metal powder of said preceding layer comprises applying an adhesive to the preceding layer.
3. A method as claimed in claim 2 further comprising subsequently applying a solvent, heat and/or electromagnetic energy to the adhesive to release the adhesive at the interface.
4. A method as claimed in claim 1 further comprising subsequently separating the un-fused metal powder of the preceding layer from the fused metal powder.