Partial solvent stripping process for recovering brominated butadiene polymers from solution
View Patent ↗Brominated butadiene polymers are recovered from a bromination reaction solution by partially stripping the solvent to form a concentrated solution or slurry, and then recovering the brominated butadiene polymer from the concentrated solution or slurry. The process allows for a simplified, effective an economical recovery of the brominated butadiene polymer. Brominated butadiene polymers recovered in this manner are often very thermally stable.
1. A process comprising
a) brominating a butadiene polymer to form a crude reaction mixture containing a brominated butadiene polymer dissolved or dispersed in a solvent;
b) distilling a portion of the solvent from the crude reaction mixture to form (1) a distillate containing a portion of the solvent and (2) a concentrated solution or slurry of the brominated butadiene polymer in another portion of the solvent, such that from about 20 to 70% of the solvent is removed from the crude reaction mixture to produce a concentrated solution or slurry that contains from 65 to 80 percent by weight of the solvent, and then
c) recovering the brominated butadiene polymer from the concentrated solution or slurry by (1) precipitating the brominated butadiene polymer from the concentrated solution or slurry by contact with an antisolvent, (2) thermally stripping the remaining solvent from the concentrated solution or slurry by forming the concentrated solution or slurry into droplets and heating the droplets to a temperature sufficient to drive off most or all of the remaining solvent, (3) a combination of both (1) and (2), or (4) a combination of (1), (2) or (3) with a washing step.
2. The process of claim 1 , wherein step a) is conducted by brominating the butadiene polymer with elemental bromine in the presence of the solvent and an aliphatic alcohol having a boiling temperature of up to 120° C.
3. The process of claim 2 , wherein in step b), a distillate is formed and condensed, and the condensed distillate phase separates into a solvent layer and a layer that contains at least a portion of the aliphatic alcohol.
4. The process of claim 1 , wherein the butadiene polymer is a copolymer of butadiene and a vinyl aromatic polymer.
5. The process of claim 4 , wherein the copolymer is a block copolymer of butadiene and styrene.
6. The process of claim 1 , wherein the butadiene polymer is a butadiene homopolymer.
7. The process of claim 1 , wherein the brominated polybutadiene polymer is recovered in the form of particles having a bulk density of at least 0.20 g/mL.
8. The process of claim 1 , wherein the brominated polybutadiene polymer is recovered in the form of particles having a bulk density of at least 0.35 g/mL.
9. The process of claim 1 , wherein the brominated polybutadiene polymer is recovered in the form of particles having a bulk density of 0.40-0.45 g/mL.