Precipitated silicas for storage-stable RTV-1 silicone rubber formulations without stabilizer

1. A sealant comprising:

a one component room-temperature vulcanizing silicone rubber composition (RTV-1K); and

a precipitated silica; wherein

the precipitated silica has physiochemical properties comprising:

an SiOH isolated absorbance ratio of from 1.5 to 10,

a silanol group density of 1 to 3.0 SiOH/nm 2 ,

a modified tapped density of 1 to 50 g/l, and

a pH of 3 to 5, wherein the pH is measured as a aqueous suspension of 5.00 g of the precipitated silica in 100 ml. of deionized water, and

wherein the sealant is free of a stabilizer and is storage-stable for 35 days when stored at 50° C.

2. The sealant according to claim 1 , further comprising a crosslinking system selected from the group consisting of an acetoxy-crosslinking, an alkoxy-crosslinking and an oxime-crosslinking system.

3. The sealant of claim 1 , wherein

the pH of the precipitated silica is from 3 to less than 4.

4. The sealant of claim 1 , wherein

a BET surface area of the precipitated silica is from 50-600 m 2 /g,

a CTAB surface area of the precipitated silica is from 50-350 m 2 /g, and

a DBP (anhydrous) value of the precipitated silica is from 150-400 g/100 g.

5. The sealant of claim 1 , wherein

30% to 100% of the particles in a volume-based particle distribution curve of the precipitated silica are less than 1 μm and/or

a d90 value of the volume-based particle distribution curve is not greater than 0.001-10 μm.

6. The sealant of claim 1 , wherein a particle distribution curve of the precipitated silica is bimodal.

7. The sealant of claim 1 , wherein

a loss on ignition of the precipitated silica is is 0.1%-3.0% by weight and/or

a loss on drying of the precipitated silica is is 0.1%-3.0% by weight.

8. The sealant of claim 1 , wherein

the precipitated silica is hydrophilic.

9. A process for preparing the precipitated silica of the sealant according to claim 1 , comprising:

1) reacting at least one silicate with at least one acidifier;

2) filtering and washing the resulting precipitated silica;

3) drying the resulting precipitated silica or filtercake;

4) optionally grinding the precipitated silica obtained after 3);

5) heat-treating the dried and/or ground precipitated silica; and

6) optionally grinding the precipitated silica obtained after 5);

wherein

after 3) and/or 4) and/or 5) and/or 6) at least one acidifier is added to obtain the precipitated silica having a pH of 3-5, when the pH is measured as a aqueous suspension of 5.00 g of the precipitated silica in 100 ml. of deionized water.

10. The process according to claim 9 , wherein the reacting at least one silicate with at least one acidifier comprises:

1a) preparing an initial charge of water or of water and at least one silicate and/or a silicate solution, wherein the pH of the resulting initial charge is between 5 and 10 and the temperature of the initial charge is between 80 and 100° C.;

1b) metering at least one silicate and/or a silicate solution and at least one acidifier into the initial charge from 1a) with stirring at 80 to 100° C. until the solids content of the precipitation suspension reaches a level which leads to the solids content which is to be reached in 1c);

1c) adding an acidifier at a temperature of the precipitation suspension of 80 to 100° C., to lower the pH of the precipitation suspension to 2 to 6;

wherein

a solids content of the precipitation suspension at the end of the addition of the acidifier is between 30 and 70 g/l.

11. The process according to claim 10 , wherein during the metering at least one silicate and/or a silicate solution and at least one acidifier into the initial charge from 1a) the pH is held constant at a level between 7 and 10.

12. The process according to claim 9 , wherein in the optional grinding, the grinding parameters are selected to obtain a ground product having a fine-particle fraction of 5% to 100% in the range <1 μm of the volume-based particle distribution and/or a d90 value of the volume-based particle distribution curve of between 0.001 and 10 μm.

13. The process according to claim 12 , wherein the grinding takes place in a fluid-bed opposed-jet mill.

14. The process according to claim 13 , wherein steam is an operational medium in the fluid-bed opposed-jet mill.

15. The process according to claim 12 , further comprising:

before the actual operation with the operational medium, heating the grinding chamber and/or at the mill outlet to a temperature that is higher than the dew point of the vapor and/or operational medium,

wherein

the grinding is carried out in a grinding apparatus comprising a jet mill, and the grinding phase in the mill is an operational medium selected from the group consisting of a gas, steam, and a mixture of a gas and steam.

16. The process according to claim 9 , wherein the heat treatment of the dried and/or precipitated silica is carried out in a fluidized-bed, fluid-bed or rotary-tube reactor.

17. The process according to claim 16 , wherein the heat treatment is carried out in a fluidized-bed reactor and further comprising:

5a) introducing the precipitated silica into the fluidized-bed reactor;

5b) preheating the reactor to 300 to 800° C., the reactor being traversed at the same time by a flow of inert gas and/or nitrogen/air mixture in such a way as to produce a fluidization velocity of 0.02 to 0.06 m/s;

5c) feeding in a gas mixture I comprising steam and an inert gas, or a gas mixture II comprising steam, an inert gas and air, at 300 to 800° C. for a period of 0.25 to 6 h, the gas mixture traversing the reactor with a fluidization velocity of 0.02 to 0.06 m/s, and the gas mixtures I and II having a steam concentration of 10 to 95% by volume and in the case of gas mixture II an oxygen content of 0.01% to 21% by volume;

5d) interrupting the addition of vapor and expelling the vapor by adding an inert gas and/or an inert gas/air mixture at 300 to 800° C., the gas or gas mixture traversing the reactor with a fluidization velocity of 0.02 to 0.06 m/s, and, if using an inert gas/air mixture, said mixture having an oxygen content of 0.01% to 21% by volume; and

5e) cooling the heat-treated precipitated silica to room temperature in a dry process atmosphere, where, if using an inert gas/air mixture, said mixture has an oxygen content of 0.01% to 21% by volume.

18. The process according to claim 9 , wherein the at least one acidifier is a gaseous acidifier selected from the group consisting of HCl, HBr, an oxide of nitrogen, vaporized SO 3 , and vaporized SOCl 2 .

19. The process according to claim 18 , further comprising flushing the precipitated silica with an inert gas and/or dry air after the acidification.

20. The process according to claim 9 , wherein

the precipitated silica obtained after 5 and/or 6 is divided into a fraction A and fraction B,

the fraction A is acidified to pH of 2 to 4.5 using a gaseous acidifier, and thereafter the acidified fraction A is mixed with fraction B to obtain the precipitated silica having a pH of 3-5, when the pH is measured as a aqueous suspension of 5.00 g of the precipitated silica in 100 ml. of deionized water.

21. The process according to claim 20 , wherein the acidified fraction A is flushed with an inert gas and/or dry air after the acidification.

22. A method for the preparation of the sealant of claim 1 , comprising adding a precipitated silica to a room-temperature vulcanizing (RTV-1K) silicone rubber;

wherein

no stabilizer is added to the sealant,

the precipitated silica has physiochemical properties comprising:

an SiOH isolated absorbance ratio of from 1.5 to 10,

a silanol group density of 1 to 3.0 SiOH/nm 2 ,

a modified tapped density of 1 to 50 g/l, and

a pH of 3 to 5, wherein the pH is measured as a aqueous suspension of 5.00 g of the precipitated silica in 100 ml. of deionized water.

23. The method according to claim 22 , further comprising adding a crosslinking system to the sealant, wherein the crosslinking system is selected from the group consisting of an acetoxy-crosslinking, an alkoxy-crosslinking and an oxime-crosslinking system.

24. An industrial method comprising applying the sealant according to claim 1 to a substrate, wherein the industrial method is one selected from the group consisting of sealing a joint in a building, adhesively attaching parts of a automobile and coating a textile fabric.