Polypropylene fiber for reinforcement of matrix materials
View Patent ↗Disclosed are structural materials including polymeric reinforcement fibers that can provide added strength and fracture toughness to the matrix. The polymeric reinforcement fibers are polypropylene-based monofilament fibers or tape fibers exhibiting extremely favorable mechanical characteristics for structural reinforcement including modulus greater than 12 MPa and elongation less than about 10%. The disclosed reinforced composite materials can exhibit desired average residual strength values with less total fiber loading necessary to attain the ARS values as compared to previously known polymer reinforced materials. Very high strength and fracture toughness can be attained in the disclosed composite materials.
1. A composite material comprising:
a matrix material;
a plurality of discrete fibers comprising polypropylene dispersed throughout the matrix material, wherein fibers describe an elastic modulus greater than about 10 GPa and an elongation less than about 10%, the fibers defining an axial length of less than about 5 inches;
wherein the composite material has an average residual strength of greater than 0.80 MPa at a fiber loading value of between about 2 and about 4 pounds of fibers per cubic yard of matrix material.
2. The composite material of claim 1 , wherein the fibers describe an elastic modulus greater than about 12 GPa.
3. The composite material of claim 1 , wherein the fibers describe an elongation less than about 8%.
4. The composite material of claim 1 , wherein the matrix material is an inorganic matrix material.
5. The composite material of claim 4 , wherein the matrix material is a concrete.
6. The composite material of claim 4 , wherein the matrix material comprises gypsum.
7. The composite material of claim 1 , wherein the composite material describes an average residual strength greater than 1.75 MPa.
8. The composite material of claim 1 , wherein the composite material describes an average residual strength greater than 1.80 MPa.
9. The composite material of claim 1 , wherein the composite material comprises the multitude of fibers at a fiber loading level of less than or equal to about 18 pounds of fibers per cubic yard of matrix material.
10. The composite material of claim 1 , wherein the fibers describe an elastic modulus greater than or equal to about 18 GPa.
11. The composite material of claim 1 , wherein the polymeric component of the fibers is a polypropylene/polyethylene blend.
12. The composite material of claim 1 , wherein the polymeric component of the fibers is a polypropylene homopolymer or copolymer.
13. The composite material of claim 1 , wherein the fibers comprise monofilament fibers.
14. The composite material of claim 1 , wherein the fibers comprise tape fibers.
15. The composite material of claim 1 , wherein the fibers comprise fibrillated fibers.
16. The composite material of claim 1 , wherein the fibers comprise deformed fibers.
17. The composite material of claim 1 , wherein the fibers comprise fibers defining a length of less than about 3 inches.
18. The composite material of claim 1 , the material further comprising a second plurality of discrete fibers, the second plurality of discrete fibers being selected from the group consisting of steel fibers, carbon fibers, poly-paraphenylene terephthalamide fibers, ultra-high molecular weight polyethylene fibers, liquid crystal fibers, polyvinyl alcohol fibers, and glass fibers.
19. The composite material of claim 1 , wherein the material has a compressive strength greater than about 50 MPa.
20. A composite material comprising:
a matrix material; and
a plurality of discrete polypropylene homopolymer monofilament fibers dispersed throughout the matrix material, wherein the polypropylene fibers have a ratio of equatorial intensity to meridonal intensity greater than about 1.0 according to SAXS measuring techniques, the fibers defining an axial length of less than about 5 inches.
21. The composite material of claim 20 , wherein the polypropylene fibers possess greater than about 80% crystallinity according to WAXS measuring techniques.
22. The composite material of claim 20 , wherein the polypropylene fibers describe an elongation less than about 10%.
23. The composite material of claim 20 , wherein the matrix material is a concrete.
24. The composite material of claim 20 , wherein the matrix material is gypsum.
25. The composite material of claim 20 , wherein the polypropylene fibers have a ratio of equatorial intensity to meridonal intensity greater than about 1.5 according to SAXS measuring techniques.
26. The composite material of claim 20 , wherein the polypropylene fibers have a ratio of equatorial intensity to meridonal intensity greater than about 3.0 according to SAXS measuring techniques.
27. The composite material of claim 20 , wherein the polypropylene fibers are fibrillated or deformed.
28. The composite material of claim 20 , wherein the composite material describes an average residual strength greater than or equal to 2 MPa at a fiber loading value of less than 14 pounds of fibers per cubic yard of matrix material.
29. The composite material of claim 20 , wherein the composite material has a compressive strength of greater than about 50 MPa.
30. A method of forming a composite material comprising:
providing a plurality of discrete polypropylene fibers defining an axial length of less than about 5 inches, wherein the fibers have a ratio of equatorial intensity to meridonal intensity greater than about 1.0 according to SAXS measuring techniques;
combining the plurality of discrete polypropylene fibers with a matrix material such that the fibers are dispersed throughout the matrix material to form a composite material comprising the matrix material and the polypropylene fibers; and
curing the composite material.
31. The method of claim 30 , wherein the fibers describe an elastic modulus greater than about 10 GPa and an elongation less than about 10%.
32. The method of claim 30 , wherein the matrix material is an inorganic matrix material.
33. The method of claim 32 , wherein the matrix material is a concrete.
34. The method of claim 32 , wherein the matrix material comprises gypsum.
35. The method of claim 30 , wherein the composite material describes an average residual strength greater than 1.75 MPa.
36. The method of claim 30 , wherein the composite material describes an average residual strength greater than 1.80 MPa.
37. The method of claim 30 , wherein the composite material comprises the plurality of fibers at a fiber loading level of less than or equal to about 18 pounds of 15 fibers per cubic yard of matrix material.
38. The method of claim 30 , wherein the polymeric component of the polypropylene fibers is formed from polypropylene homopolymers, polypropylene copolymers, or mixtures thereof.
39. The method of claim 30 , wherein the polymeric component of the polypropylene fibers is formed from a blend of polypropylene and a second polyolefin.
40. The method of claim 30 , the method further comprising combining the plurality of discrete polypropylene fibers and the matrix material with a second plurality of fibers.
41. The method of claim 40 , wherein the second plurality of fibers is selected from the group consisting of steel fibers, carbon fibers, poly-paraphenylene terephthalamide fibers, ultra-high molecular weight polyethylene fibers, liquid crystal fibers, polyvinyl alcohol fibers, and glass fibers.
42. The method of claim 30 , further comprising deforming the fibers during the step of combining the polypropylene fibers with the matrix material.