Method for manufacturing magnetic recording media
View Patent ↗A method for manufacturing discrete track media and patterned media is disclosed which enables a magnetic recording layer having excellent magnetic characteristics to be obtained without imparting damage to a crystal orientation control layer which is at the surface when forming the magnetic recording layer. The method for manufacturing magnetic recording media comprises a process of forming a soft magnetic layer on a substrate; a process of forming a first crystal orientation control layer on the soft magnetic layer; a process of providing a depression in at least a portion of the first crystal orientation control layer; a process of performing heat treatment of the first crystal orientation control layer; and a process of forming a magnetic recording layer on the first crystal orientation control layer.
1. A method for manufacturing magnetic recording media, comprising the steps of:
(a) forming a soft magnetic layer on a substrate;
(b) forming a first crystal orientation control layer on the soft magnetic layer;
(c) providing depressions in the first crystal orientation control layer according to a placement interval;
(d) performing heat treatment of the first crystal orientation control layer; and
(e) forming a magnetic recording layer on the first crystal orientation control layer,
wherein step (c) is performed after step (b) and before steps (d) and (e).
2. A method for manufacturing magnetic recording media, comprising the steps of
(a) forming a soft magnetic layer on a substrate;
(b) forming a first crystal orientation control layer on the soft magnetic layer;
(c) providing depressions in the first crystal orientation control layer according to a placement interval;
(d) performing heat treatment of the first crystal orientation control layer;
(e) forming a second crystal orientation control layer; and
(f) forming a magnetic recording layer on the first crystal orientation control layer,
wherein step (c) is performed after step (b) and before steps (d), (e), and (f), and
wherein step (d) is performed before steps (e) and (f).
3. The method for manufacturing magnetic recording media according to claim 1 , wherein the depressions in the first crystal orientation control layer have a depth of 1 nm to 12 nm.
4. The method for manufacturing magnetic recording media according to claim 2 , wherein the depressions in the first crystal orientation control layer have a depth of 1 nm to 12 nm.
5. The method for manufacturing magnetic recording media according to claim 1 , wherein said method does not include removal of the magnetic recording layer to form depressions.
6. The method for manufacturing magnetic recording media according to claim 1 , wherein said method does not include removal of the soft magnetic recording layer to form depressions.
7. The method for manufacturing magnetic recording media according to claim 5 , wherein said method does not include removal of the soft magnetic recording layer to form depressions.
8. The method for manufacturing magnetic recording media according to claim 1 , wherein a nanoimprinting method is used to produce the depressions in the first crystal orientation control layer.
9. The method for manufacturing magnetic recording media according to claim 1 , wherein step (c) comprises applying and patterning a resist layer.
10. The method for manufacturing magnetic recording media according to claim 9 , wherein said resist layer is patterned by a nanoimprinting method.
11. The method for manufacturing magnetic recording media according to claim 9 , wherein said resist layer is patterned by actinic radiation.
12. The method for manufacturing magnetic recording media according to claim 8 , wherein the nanoimprinting method produces the depressions in the first crystal orientation directly.