View Patent ↗The present disclosure relates to a near metallic glass based alloy wherein the alloy includes at least 40 atomic percent iron, greater than 10 atomic percent of at least one or more metalloids, and less than 50 atomic percent of at least two or more transition metals, wherein one of said transition metals is Mo said alloy exhibits a tensile strength of 2400 MPa or greater and an elongation of greater than 2%.
1. A near metallic glass based alloy, comprising:
an alloy including Fe present in the range of 48 to 52 atomic %, Mn present in the range of 0.1 to 3.0 atomic %, Cr present in the range of 17 to 20 atomic %, Mo present in the range of 5 to 7 atomic %, W present in the range of 1 to 3 atomic %, B present in the range of 14 to 17 atomic %, C present in the range of 3 to 5 atomic percent and Si present in the range of 1 to 4 atomic % and said alloy exhibits a tensile strength of 2400 MPa or greater and an elongation of greater than 2%.
2. The near metallic glass based alloy of claim 1 , wherein said alloy consists of Fe present in the range of 48 to 52 atomic %, Mn present in the range of 0.1 to 3.0 atomic %, Cr present in the range of 17 to 20 atomic %, Mo present in the range of 5 to 7 atomic %, W present in the range of 1 to 3 atomic %, B present in the range of 14 to 17 atomic %, C present in the range of 3 to 5 atomic percent and Si present in the range of 1 to 4 atomic %.
3. The near metallic glass based alloy of claim 1 , wherein said alloy composition comprises Fe 50.8 Mn 1.9 Cr 18.4 Mo 5.4 W 1.7 B 15.5 C 3.9 Si 2.4 .
4. The near metallic glass based alloy of claim 1 , wherein said alloys exhibit one or more crystallization transformation peaks at temperatures of greater than 625° C.
5. The near metallic glass based alloy of claim 1 , wherein said alloy exhibits crystallization transformation peaks at temperatures in the range of 625° C. to 800° C.
6. The near metallic glass based alloy of claim 1 , wherein said alloy exhibits elongation in the range of greater than 2% to 8%.
7. The near metallic glass based alloy of claim 1 , wherein said alloy exhibits a tensile strength of 2400 to 2850 MPa.