Undercoating layers providing improved topcoat functionality
View Patent ↗A coated article includes a substrate and a first coating formed over at least a portion of the substrate. The first coating includes a mixture of oxides including oxides of at least two of P, Si, Ti, Al and Zr. A functional coating is formed over at least a portion of the first coating. In one embodiment, the functional coating includes fluorine doped tin oxide. In another embodiment, the functional coating includes titania.
1. A coated article, comprising:
a substrate;
a first coating formed over at least a portion of the substrate, the first coating comprising at least two oxides selected from the group consisting of oxides of P, Si, Ti, Al and Zr; and
a functional coating formed over at least a portion of the first coating,
wherein the first coating is a multi-layer coating comprising:
a first layer comprising phosphorous oxide, silica, and titania, with titania present in the range of 10-25 volume %;
a second layer comprising phosphorous oxide, silica, and titania, with titania present in the range of 36-50 volume %; and
a third layer comprising phosphorous oxide, silica, and titania, with titania present in the range of 9-25 volume %.
2. The article of claim 1 , wherein the first coating further comprises an oxide of Al.
3. The article of claim 1 , wherein the functional coating comprises at least one oxide selected from the group consisting of oxides of Ti, Zn, Fe, Mn, Al, Ce, Sn, Sb, Hf, Zr, Ni, Zn, Bi, Ti, Co, Cr, Si, In, and an alloy of two or more of these materials.
4. The article of claim 3 , wherein the functional coating comprises at least one dopant selected from F, In, Al and Sb.
5. The article of claim 4 , wherein the functional coating comprises fluorine doped tin oxide.
6. The article of claim 4 , wherein the functional coating comprises titania.
7. The article of claim 6 , wherein the titania has a thickness in the range of 113 nm to 121 nm.
8. The article of claim 1 , wherein the article has a color in the range of −10≦a* ≦2 and −15≦b*≦0.
9. The article of claim 8 , wherein the article has an a* in the range of −8 to −4.4, a b* in the range of −12.6 to −5.2, and an L* in the range of 50.5 to 52.3.
10. A coated article, comprising:
a substrate;
a first coating formed over at least a portion of the substrate, the first coating comprising oxides of at least two of P, Si, Ti, Al and Zr; and
a functional coating formed over at least a portion of the first coating,
wherein the first coating is a multi-layer coating comprising:
a first layer comprising 5-10 volume % phosphorous oxide, 70-80 volume % silica and 10-25 volume % titania with a thickness in the range of 11 nm to 29 nm;
a second layer comprising 2 volume % phosphorous oxide, 48-62 volume % silica and 36-50 volume % titania with a thickness in the range of 21 nm to 33 nm; and
a third layer comprising 5-11 volume % phosphorous oxide, 70-80 volume % silica and 9-25 volume % titania with a thickness in the range of 15 nm to 23 nm.
11. A coated article, comprising:
a glass substrate;
a first coating formed over at least a portion of the substrate, the first coating comprising at least two oxides selected from the group consisting of oxides of P, Si, Ti, Al and Zr; and
a functional coating formed over at least a portion of the first coating, the functional coating comprising an oxide selected from the group consisting of titania and fluorine doped tin oxide,
wherein the first coating is a multi-layer coating comprising,
a first layer comprising phosphorous oxide, silica, and titania, with silica present in the range of 70-80 volume %;
a second layer comprising phosphorous oxide, silica, and titania, with silica present in the range of 48-62 volume %; and
a third layer comprising phosphorous oxide, silica, and titania, with silica present in the range of 70-80 volume %.