Poly(arylene ether) composition and a covered conductor with flexible covering wall and large size conductor
View Patent ↗Disclosed herein is covered conductors with a normal to large conductor cross-section area (AWG 5 to AWG 24). The thickness of the coating can be, for example, 0.25 to 8.0 millimeter (mm). Also disclosed are a thermoplastic composition comprising a poly(arylene ether) having an intrinsic viscosity greater than 0.25 dl/g as measured in chloroform at 25° C., a styrenic resin, a polyolefin resin, and optionally a flame retardant, a compatibilizer, or a combination of a flame retardant and a compatibilizer. The coating comprises the thermoplastic composition described above.
1. A thermoplastic composition comprising: 35 to 45 weight percent of a poly(arylene ether) having an intrinsic viscosity greater than 0.25 dl/g as measured in chloroform at 25° C., 5 to 30 weight percent of a styrenic resin, and 20 to 45 weight percent of a polyolefin resin comprising a mixture of medium density polyethylene and a high density polyethylene, wherein weight percent is based on the total weight of the composition, the thermoplastic composition has a flexural modulus of 400-1000 Megapascals (MPa) as determined by ASTM D790-03, and comprises a continuous polyolefin phase and dispersed poly(arylene ether) particles and the poly(arylene ether) particles have an average diameter less than 5 micrometers.
2. The thermoplastic composition of claim 1 further comprising a flame retardant, a compatibilizer, or a combination of a flame retardant and a compatibilizer, wherein the compatibilizer is different from the styrenic resin.
3. The thermoplastic composition of claim 1 , wherein the styrenic resin is a hydrogenated styrenic block copolymer having a poly(alkenyl aromatic) content of 10 to 45 weight percent.
4. A covered conductor comprising: a conductor and a covering disposed over the conductor, wherein the covering comprises a thermoplastic composition and the thermoplastic composition comprises 35 to 45 weight percent of a poly(arylene ether) having an intrinsic viscosity greater than 0.25 dl/g as measured in chloroform at 25° C., a styrenic resin, 5 to 30 weight percent of a polyolefin resin comprising a mixture of medium density polyethylene and a high density polyethylene selected from the group consisting of high density polyethylene and combinations of high density polyethylene, wherein weight percent is based on the total weight of the composition and the thermoplastic composition has a flexural modulus of 400-1000 Megapascals (MPa) as determined by ASTM D790-03 and comprises a continuous polyolefin phase and dispersed poly(arylene ether) particles and the poly(arylene ether) particles have an average diameter less than 5 micrometers and wherein the covered conductor essentially meets the performance requirement of ISO 6722, and the conductor has a cross-section that meets as least one of following: (i) American Wire Gauge (AWG) of AWG 24 to AWG 5, (ii) a cross-section area of 0.20 to 16.8 mm 2 (corresponding to AWG 24 to AWG 5 according to ASTM B256-02); (iii) a nominal diameter from 0.51 to 4.62 mm (corresponding to AWG 24 to AWG 5 according to UL 1581, 4th edition, Table 20.1).
5. The covered conductor of claim 4 , wherein the covering has a thickness of 0.25 to 8 mm.
6. The covered conductor of claim 4 , wherein the thermoplastic composition further comprises a flame retardant, a compatibilizer, or a combination of a flame retardant and a compatibilizer wherein the compatibilizer is different from the styrenic resin.
7. The covered conductor of claim 4 , wherein the styrenic resin is a hydrogenated styrenic block copolymer having a poly(alkenyl aromatic) content of 10 to 45 weight percent.
8. An automotive wire harness assembly comprising the covered conductor of claim 4 .