Preparation method of catalyst for ethylene polymerization and copolymerization
Provided is a preparation method of a catalyst for ethylene (co)polymerization, comprising the following steps: (1) preparing a magnesium compound solution by contact-reacting a halogenated magnesium compound with a mixed solvent of cyclic ether and at least one alcohol; (2) reacting the resulted magnesium compound solution from the above step (1) with a silicon compound having at least one alkoxy group; (3) preparing a support by adding a titanium compound to the resulted product from the step (2); and (4) reacting thus obtained support with a titanium compound and optionally a monoester compound, resulting in a catalyst. Catalysts prepared according to the present invention have a regulated particle shape, and their particle size can be easily adjusted. Therefore, with such catalyst, it is possible to produce polymers having high bulk density at high production yield.
1. A method of preparing a catalyst for ethylene polymerization or copolymerization, characterized by comprising the following steps:
(1) preparing a magnesium compound solution by contact-reacting a halogenated magnesium compound with a mixed solvent of cyclic ether and at least one alcohol;
(2) reacting the resulted magnesium compound solution from the above step (1) with a silicon compound having at least one alkoxyl group;
(3) preparing a support by adding a titanium compound represented by a general formula (I) to the resulted product from the step (2):
Ti(OR) a X (4-a) (I)
wherein R is an alkyl group having C 1-10 ; X is a halogen atom; and a is an integer of 0-4; and
(4) reacting the obtained support with a titanium compound and a monoester compound represented by a general formula of R 1 COOR 2 , wherein R 1 and R 2 are independently an alkyl or aromatic group having C 1-25 , resulting in a catalyst.
2. The method according to claim 1 , wherein, in the step (1), the cyclic ether is tetrahydrofuran or 2-methyl tetrahydrofuran, and the alcohol is a mono- or polyvalent alcohol having 1-20 carbon atoms.
3. The method according to claim 1 , wherein the amount of the mixed solvent in step (1) is 1-20 moles based on one mole of the halogenated magnesium compound.
4. The method according to claim 1 , wherein the silicon compound having at least one alkoxy group in the step (2) has a general formula of R n Si(OR 1 ) 4-n , wherein R and R 1 are independently hydrocarbon having C 1-12 , and n is an integer of 0-3.
5. The method according to claim 1 , wherein the amount of the monoester compound is 0.01-500 moles based on one mole of the halogenated magnesium compound.
6. The method according to claim 1 , wherein, in the step (1), the cyclic ether is tetrahydrofuran or 2-methyl tetrahydrofuran, and the alcohol is a mono- or polyvalent alcohol having 1-20 carbon atoms.
7. The method according to claim 1 , wherein the amount of the mixed solvent in step (1) is 1-20 moles based on one mole of the halogenated magnesium compound.
8. The method according to claim 1 , wherein the silicon compound having at least one alkoxy group in the step (2) has a general formula of R n Si(OR 1 ) 4-n , wherein R and R 1 are independently hydrocarbon having C 1-12 , and n is an integer of 0-3.