Polyestercarbonate copolymers with high scratch resistance
View Patent ↗Disclosed are polyestercarbonate copolymers comprising a carbonate unit of Formula (I), an ITR ester unit of Formula (V), and optionally a different carbonate unit of Formula (VI): wherein R a , R b , p, q, A, h, j, k, R c , r, and R 1 are as described herein. The polyestercarbonate copolymers have a combination of scratch resistance, good flow, and good weatherability.
1. An article formed from a polyestercarbonate terpolymer, the terpolymer comprising:
from about 30 to about 90 mole percent of a DMBPC unit of Formula (III):
from about 5 to about 50 mole percent of an ITR ester unit of Formula (V):
wherein h corresponds to the molar percentage of the isophthalate, j corresponds to the molar percentage of the resorcinolate, and k corresponds to the molar percentage of the terephthalate; h, j, and k add up to 100 mole percent of the ester unit; each R c is independently selected from C 1-12 alkyl and halogen; and r is an integer from zero to 3;
from about 5 to about 25 mole percent of a bisphenol A unit of Formula (VII):
wherein the polyestercarbonate terpolymer has a scratch resistance of 15 micrometers or less, when measured using the Erichson Scratch Test with a 6N load; and a haze level below 5 and a light transmittance greater than 75%, as measured by ASTM D1003;
wherein the terpolymer is formed by mixing the DMPBC unit, the ITR ester unit, the bisphenol-A unit, and a chain transfer catalyst to form a mixture, wherein the chain transfer catalyst is present in the mixture in the amount of from 300 ppm to 400 ppm, and reacting the mixture to form the terpolymer.
2. The article of claim 1 , wherein the polyestercarbonate terpolymer has a total color shift dE* of 12 or less after 500 hours exposure, according to ASTM D2244.
3. The article of claim 1 , wherein the polyestercarbonate terpolymer has a gloss of 40 or higher when measured according to ASTM D523 after 1000 hours weathering according to SAE J1885.
4. The article of claim 1 , wherein the polyestercarbonate terpolymer has a gloss of 90 or higher when measured according to ASTM D523 after 1000 hours weathering according to SAE J1960.
5. The article of claim 1 , wherein the polyestercarbonate terpolymer has a melt volume rate of 25 cc/10 minutes or less, according to ASTM D1238.
6. A method of preparing a polyestercarbonate terpolymer, comprising:
providing a polycarbonate polymer of Formula (IX) and a polyestercarbonate polymer of Formula (X):
wherein each R a and R b is independently halogen or hydrocarbon; p and q are independently integers from 1 to 4; A is selected from C 1 -C 12 alkyl, C 6 -C 20 aromatic, and C 6 -C 20 cycloaliphatic; and w is the degree of polymerization;
wherein R 1 , R 2 , and T are independently divalent organic radicals; m is the molar percentage of carbonate units; and n is the molar percentage of ester units;
mixing the polycarbonate polymer, the polyestercarbonate polymer, and a chain transfer catalyst to form a mixture, wherein the chain transfer catalyst is present in the mixture in the amount of from 300 ppm to 400 ppm; and
reacting the mixture to form the polyestercarbonate terpolymer;
wherein the polyestercarbonate terpolymer has a scratch resistance of 15 micrometers or less, when measured using the Erichson Scratch Test with a 6N load; and a haze level below 5 and a light transmittance greater than 75%, as measured by ASTM D1003.