Method for producing ceramic honeycomb structure
A method for producing a ceramic honeycomb structure comprising the steps of mixing and blending at least a ceramic material and a pore-forming material to form a moldable material, extrusion-molding the moldable material, and drying and sintering the resultant molded honeycomb article, the amount of the pore-forming material added being adjusted depending on the packed bulk density of the pore-forming material.
1. A method for producing ceramic honeycomb structures having a pore volume comprising the steps of
mixing and blending ceramic material powder with a pore-forming material composed of microcapsules A to form a moldable material, extrusion-molding the moldable material to form a ceramic honeycomb article, and drying and sintering the resultant molded honeycomb article to form a honeycomb structure A,
mixing and blending ceramic material powder with a pore-forming material composed of microcapsules B to form a second moldable material, extrusion-molding the second moldable material to form a second ceramic honeycomb article, and drying and sintering the resultant second molded honeycomb article to form a honeycomb structure B,
wherein said pore-forming material consists essentially of foamed resin microcapsules constituted by a resin shell containing a gas, and
wherein said microcapsules A are added to produce said honeycomb structure A in an amount M 1 (% by mass) and said microcapsules B are added to produce said honeycomb structure B in an amount M 2 (% by mass),
wherein said honeycomb structure B has the same pore volume as said honeycomb structure A,
wherein said microcapsules A have a packed bulk density Q 1 (g/cm 3 ) and said microcapsules B have a packed bulk density Q 2 (g/cm 3 ), such that Q 1 is not equal to Q 2 , and
wherein
M 2 >M 1 , when Q 1 >Q 2 , and
M 2 <M 1 , when Q 1 <Q 2 .
2. The method for producing ceramic honeycomb structures having a pore volume according to claim 1 ,
wherein the microcapsules comprise a mixture of at least two types of microcapsules having different packed bulk densities, wherein the mixture of at least two types of microcapsules have an adjusted packed bulk density.
3. The method for producing ceramic honeycomb structures having a pore volume according to claim 1 ,
wherein the microcapsules have a packed bulk density of 0.13 to 0.17 g/cm 3 at a compression force of 0.13 MPa.
4. The method for producing ceramic honeycomb structures having a pore volume according to claim 1 , wherein the microcapsules have a specific surface area of 0.058 to 0.218 m 2 /ml.