Modifying tubular LDPE with free radical initiator
View Patent ↗A method of modifying a tubular low density polyethylene (LDPE) is disclosed. In the method ethylene is polymerized with a free radical initiator in a high pressure reactor to form an LDPE. The LDPE is then reacted with a free radical initiator to produce a modified polyethylene. The modified polymer has an increased long chain branching index as indicated by the increase in the gel permeation chromatography branching index.
1. A process comprising polymerizing ethylene in a high pressure tubular reactor to produce a LDPE, degassing the LDPE in a high pressure separator, and extruding the LDPE to form pellets, wherein a free radical initiator is mixed and reacted with the LDPE after it is discharged from the tubular reactor but before the extrusion, and wherein the free radical initiator is mixed with the LDPE in the high pressure separator, wherein the LDPE that has been mixed and reacted with free radical initiator has at least a 5% increase in gel permeation chromatography branching index (gpcBR) compared with the LDPE that has not been mixed and reacted with free radical initiator.
2. The process of claim 1 , wherein the free radical initiator is used in an amount within the range of about 50 ppm to about 5000 ppm of the LDPE.
3. The process of claim 1 , wherein the reaction of the LDPE with the free radical initiator is performed at a temperature within the range of about 100° C. to about 350° C.
4. The process of claim 3 , wherein the reaction temperature is within the range of about 150° C. to about 250° C.
5. The process of claim 1 , wherein the LDPE has at least a 10% increase in gpcBR.
6. The process of claim 1 , wherein the LDPE has at least 15% increase in gpcBR.
7. The process of claim 1 , wherein the free radical initiator is a peroxide selected from the group consisting of dicumyl peroxide, di-t-butyl peroxide, cumyl hydroperoxide, t-butyl hydroperoxide, 2,5-dimethyl-2,5-di-t-butylperoxy hexyne, and mixtures thereof.
8. The process of claim 1 , wherein the free radical initiator is used in an amount within the range of about 500 to about 4000 ppm of the LDPE.