Polyacetal compositions with improved tribological properties
View Patent ↗The invention relates to polyacetal compositions comprising a mixture of (i) a polyacetal resin, (ii) p-aramid particles and (III) a vinyl-terminated dimethyl siloxane polymer. These compositions are useful in preparing molded articles exhibiting a good balance between high self-lubricating properties and wear resistance, and especially useful in articles that are in motion with respect to other parts they are in contact with.
1. A polyacetal composition comprising:
i. 75 wt-% to 98 wt-% of a polyacetal resin;
ii. 1 wt-% to 20 wt-% of p-aramid particles having an average largest dimension that does not exceed 500 μm; and
iii. 0.5 wt-% to 5 wt-% of a vinyl-terminated dimethyl siloxane polymer having a viscosity from 150 CST to 10,000 CST at 25° C.;
with the proviso that the p-aramid particles of (ii) excludes aramids in the form of spun filaments, woven or nonwoven fabrics, or aramid papers.
2. The polyacetal composition of claim 1 , wherein the p-aramid particles have an average largest dimension that does not exceed 150 μm.
3. The polyacetal composition of claim 1 , wherein the p-aramid particles are poly(p-phenylene terephthalamide) particles.
4. A method of manufacturing a polyacetal polymer composition, comprising the step of mixing
(i) 75 wt-% to 98 wt-% of a polyacetal resin;
(ii) 1 wt-% to 20 wt-% of p-aramid particles having an average largest dimension that does not exceed 500 μm; and
(iii) 0.5 wt-% to 5 wt-% of a vinyl-terminated dimethyl siloxane polymer having a viscosity from 150 CST to 10,000 CST at 25° C.;
with the proviso that the p-aramid particles of (ii) excludes aramids in the form of spun filaments, woven or nonwoven fabrics, or aramid papers to provide the polyacetal polymer composition.
5. A molded article formed from the polyacetal composition described in claims 1 , 2 , or 3 .
6. The molded article according to claim 5 , which is a bearing, gear, cam, roller, sliding plats, pulley, lever, guide or a conveyor system component.
7. The molded article according to claim 6 , which is a conveyor system component.
8. A polyacetal composition comprising:
i. 75 wt-% to 98 wt-% of a polyacetal resin;
ii. 1 wt-% to 20 wt-% of p-aramid particles having an average largest dimension that does not exceed 500 μm; and
iii. 0.5 wt-% to 5 wt-% of a vinyl-terminated dimethyl siloxane polymer having a viscosity from 150 CST to 10,000 CST at 25° C.;
with the proviso that the p-aramid particles of (ii) are in powder form and which have never been spun into filaments or fibers.