Seal compositions, methods, and structures for planar solid oxide fuel cells
View Patent ↗A seal composition includes a first alkaline earth metal oxide, a second alkaline earth metal oxide which is different from the first alkaline earth metal oxide, aluminum oxide, and silica in an amount such that molar percent of silica in the composition is at least five molar percent greater than two times a combined molar percent of the first alkaline earth metal oxide and the second alkaline earth metal oxide. The composition is substantially free of boron oxide and phosphorus oxide. The seal composition forms a glass ceramic seal which includes silica containing glass cores located in a crystalline matrix comprising barium aluminosilicate, and calcium aluminosilicate crystals located in the glass cores.
1. A glass ceramic seal comprising:
silica containing glass cores located in a crystalline matrix comprising barium aluminosilicate; and
calcium aluminosilicate crystals located in the glass cores;
wherein the seal contains zero to about 0.5 molar percent of boron oxide and phosphorus oxide and wherein the seal is formed from a composition comprising barium oxide, calcium oxide, alumina and silica in an amount such that a molar percent of silica in the composition is at least 5 molar percent greater than two times a combined molar percent of the barium oxide and the calcium oxide, and the seal is located in a fuel cell stack between a surface of an interconnect and an electrolyte of a solid oxide fuel cell.
2. The seal of claim 1 , wherein a thermal expansion coefficient of the seal is between about 5×10 −6 /° C. and about 11×10 −6 /° C.
3. The seal of claim 1 , wherein the seal comprises:
between about 5 mole percent and about 20 mole percent of calcium oxide, at least a portion of which is located in the calcium aluminosilicate crystals;
between about 2 mole percent and about 20 mole percent of barium oxide, at least a portion of which is located in the barium aluminosilicate crystalline matrix;
between about 5 mole percent and about 15 mole percent of aluminum oxide, at least a first portion of which is located in the barium aluminosilicate crystalline matrix and at least a second portion of which is located in the calcium aluminosilicate crystals; and
between about 45 mole percent and about 65 mole percent of the silica, at least a first portion of which is located in the barium aluminosilicate crystalline matrix, at least a second portion of which is located in the calcium aluminosilicate crystals, and at least a third portion of which comprises the glass cores.
4. The seal of claim 3 , wherein the composition consists of barium oxide, calcium oxide, alumina and silica and the composition contains zero to about 0.5 molar percent each of other glass formers and easily reducible species.
5. The seal of claim 3 , wherein the seal comprises zero to about 0.5 molar percent of arsenic oxide, lead oxide or zinc oxide and the seal comprises zero to about 5 molar percent at least one of a fluxing agent or a bulk nucleation agent.
6. The seal of claim 1 , wherein the seal excludes boron oxide, lead oxide and zinc oxide.
7. The seal of claim 1 , wherein the seal is made by heating a green tape, glass paste or glass slurry at a temperature between 900 and 1000° C. at a rate of between 3 and 10° C. per minute to form the glass ceramic seal.