Lubricant for hot metal working and powder lubricant composition for hot metal working
View Patent ↗The present invention provides a lubricant for hot metal working which is capable of inhibiting generation of white scale, attributed to the lubricant, on the surface of a workpiece material and is capable of improving lubricity to obtain favorable appearance of the finished product. The lubricant for hot metal working comprises a silicate compound used for adding to a lubricant composition mainly containing sodium borate.
1. A method for inhibiting crystallization of a lubricant composition during the process of mandrel mill rolling for drawing-tolling a hollow shell wherein the lubricant composition contains sodium borate as a main component and is adhered to the inner surface of said hollow shell, the method comprising the step of:
adding a silicate compound to the lubricant composition.
2. The method for inhibiting crystallization of a lubricant composition according to claim 1 , wherein said silicate compound is a lamellar silicate compound.
3. A powder lubricant composition for hot metal working comprising:
a first component being one or more compounds selected from a group consisting of anhydride, pentahydrate, and decahydrate of sodium borate;
a second component comprising calcium carbonate and/or lithium carbonate;
a third component comprising fatty acid sodium salt and/or fatty acid calcium salt; and
a fourth component containing a lubricant for hot metal working comprising a silicate compound,
wherein the content ratio of each component, to total mass of said first to fourth components as 100%, is: 30 to 80 mass % of said first component; 0 to 15 mass % of said second component; 5 to 15 mass % of said third component; and 10 to 40 mass % of said fourth component.
4. The powder lubricant composition for hot metal working according to claim 3 , wherein said lubricant for hot metal working is a lubricant for hot metal working comprising a silicate compound used for hot metal working added to a lubricant composition mainly containing sodium borate.
5. The powder lubricant composition for hot metal working according to claim 3 , wherein said hot metal working is mandrel mill rolling for drawing-rolling a hollow shell and said lubricant composition is a lubricant for inner surface lubrication by adhering onto the inner surface of said hollow shell.
6. The powder lubricant composition for hot metal working according to claim 3 , wherein said silicate compound is a lamellar silicate compound.
7. A method for manufacturing seamless pipe, the method comprising the steps of:
adhering a powder lubricant composition for hot metal working according to claim 3 or 4 onto the inner surface of a hollow shell; and
drawing-rolling said hollow shell.