Process for the preparation of water-in-oil and oil-in-water nanoemulsions
Process for the preparation of a water-in-oil or oil-in-water nanoemulsion wherein the dispersed phase is distributed in the dispersing phase in the form of droplets having a diameter ranging from 1 to 500 nm, comprising: 1) the preparation of a homogeneous water/oil blend (I) characterized by an interface tension lower than 1 mN/m, comprising water in an amount of 30 to 70% by weight, at least two surface-active agents having a different HLB, selected from non-ionic, anionic, polymeric surface-active agents, said surface-active agents being present in such a quantity as to make the blend homogeneous; 2) the dilution of the blend (I) in a dispersing phase consisting of oil or water with the addition of a surface-active agent, selected from non-ionic, anionic, polymeric surface-active agents, the quantity of the dispersing phase and surface-active agent being such as to obtain a nanoemulsion having a HLB different from that of the blend (I).
1. A process for the preparation of a water-in-oil nanoemulsion wherein the dispersed phase is distributed in the dispersing phase in the form of droplets having a diameter ranging from 1 to 500 nm, said process comprising:
preparing a homogeneous water/oil blend (I) having an interface tension lower than 1 mN/m and comprising water in an amount of 30 to 70% by weight and at least two surface-active agents having a different HLB, said surface-active agents being selected from the group consisting of non-ionic surface-active agents, anionic surface-active agents, and polymeric surface-active agents, and said surface-active agents being present in an amount of from 5 to 50% by weight; and
diluting the blend (I) in a dispersing phase consisting of oil and a surface-active agent selected from the group consisting of a non-ionic surface-active agent, an anionic surface-active agent, and a polymeric surface- active agent, the quantity of the dispersing phase and the surface-active agent being sufficient to obtain a nanoemulsion having a HLB different from that of the blend (I).
2. The process according to claim 1 , wherein the quantity of dispersing phase and the surface-active agent is sufficient to obtain a nanoemulsion having a HLB lower than that of the blend (1).
3. The process according to claim 1 , wherein the homogeneous water-in-oil blend (I) is prepared by dissolving the surface-active agents in an oily phase and, when the dissolution is complete, adding water under vigorous stirring, until complete homogenization.
4. The process according to claim 1 , wherein, in the homogeneous blend (1), the weight ratio between the surface-active agents produces a HLB value higher than 8.
5. The process according to claim 4 , wherein the surface-active agents are selected from non-ionic surface-active agents and the weight ratio between the surface-active agents produces a HLB ranging from 10 to 15.
6. The process according to claim 4 , wherein the surface-active agents are selected from anionic surface-active agents and the weight ratio between the surface-active agents produces a HLB higher than 20.
7. The process according to claim 4 , wherein the weight proportion between the concentration of surface-active agents in the blend and the quantity of water/oil to be dispersed varies from 0.07 to 3.5.
8. The process according to claim 7 , wherein the weight proportion between the concentration of surface-active agents in the blend and the quantity of water/oil to be dispersed varies from 0.1 to 2.
9. The process according to claim 1 , wherein the surface-active agents having a different HLB are selected from non-ionic and polymeric surface-active agents.
10. The process according to claim 1 , wherein the surface-active agents having a different HLB are selected from the group consisting of a first surface-active agent selected from non-ionic lipophilic surface-active agents (type A), a second surface-active agent selected from non-ionic hydrophilic surface-active agents (type B), and a third surface-active agent selected from polymeric surface-active agents (type C), the composition of surface-active agents (A)+(B)+(C) having a HLB ranging from 8 to 16.
11. The process according to claim 10 , wherein the composition of surface-active agents (A)+(B)+(C) has a HLB ranging from 10 to 15.
12. The process according to claim 1 , wherein the surface-active agents having a different HLB consist of a non-ionic lipophilic surface-active agent of the group of esters of fatty acids with a HLB lower than 11, a non-ionic hydrophilic surface-active agent of the group of alkyl glucosides with a HLB higher than 11 and a non-ionic polymeric surface-active agent with a HLB varying from 4 to 14.
13. The process according to claim 1 , wherein the water-in-oil nanoemulsion is prepared by dissolving a lipophilic surface-active agent in oil and slowly adding the homogeneous blend (1) under stirring said lipophilic surface-active agent being selected from the group consisting of non-ionic surface-active agents and polymer surface-active agents.
14. The process according to claim 1 , wherein the diluting of the blend (I) is performed at a temperature ranging from 5° C. to 60° C.
15. The process according to claim 2 , wherein a quantity of dispersing phase and surface-active agent is sufficient to obtain a nanoemulsion having a HLB at least 0.5 units lower with respect to that of the blend (1).
16. The process according to claim 15 , wherein the homogeneous blend (I) comprises non-ionic and polymeric surface-active agents,
the dispersing phase consists of oil and a non-ionic surface-active agent selected from the group consisting of esters of fatty acids, and
the quantity of dispersing phase and surface-active agent is sufficient to obtain a nanoemulsion having a HLB at least 0.8-5 units lower than the blend (I).
17. A water-in-oil nanoemulsion, obtained by the process according to claim 1 , having a HLB value ranging from 6 to 14, and comprising a quantity of water which varies from 1% to 30%, total surface-active agents from 0.1% to 20%, and the complement to 100% consisting of oil.
18. The nanoemulsion according to claim 17 , having a HLB value ranging from 9 to 13, and comprising a quantity of water which varies from 5% to 25%, total surface-active agents from 1.5% to 12%, and the complement to 100% consisting of oil.
19. The process according to claim 1 , wherein the oil is selected from any polar or apolar oil.
20. The process according to claim 19 , wherein the oil is selected from the group consisting of linear hydrocarbons, branched hydrocarbons and complex hydrocarbon blends.
21. The process according to claim 20 , wherein the oil is selected from the group consisting of dodecane, diesel, kerosene, soltrol, and mineral spirits.
22. The process according to claim 1 , wherein the water is selected from the group consisting of demineralised water, saltwater, and water containing additives.
23. A method of using the nanoemulsion according to claim 17 , as additive carriers in food, the oil industry, the cosmetic and pharmaceutical industries and in the fuel sector.
24. The method according to claim 23 , wherein, in the oil industry, the additives are selected from scale inhibitors, corrosion inhibitors, wax and asphaltene inhibitors, and acid solutions.
25. The method according to claim 23 , wherein the additives are selected from additives which are different and incompatible with each other.
26. The method according to claim 25 , wherein the additives are a scale inhibitor and a wax and asphaltene inhibitor or a scale inhibitor and a corrosion inhibitor.