Dyed regenerated collagen fiber, artificial hair, and method for dye-fixing treatment of dyed regenerated collagen fiber
View Patent ↗A dyed regenerated collagen fiber of the invention is a regenerated collagen fiber dyed with a dye having an excellent dye fastness. An aspect of the invention is directed to a dyed regenerated collagen fiber including at least one kind of compound selected from the group consisting of polyalkylenepolyamine compounds, condensation compounds of polyalkylenepolyamine and dicyandiamide, and acid addition salt compounds of the condensation compounds.
1. A method for fixing a dye in a dyed regenerated collagen fiber, comprising the steps of:
dyeing a regenerated collagen fiber with an aqueous solution of least one kind of a dye selected from the group consisting of 1:1 type metal complex salt dyes, 1:2 type metal complex salt dyes and reactive dyes, and then
immersing a dyed regenerated collagen fiber in an aqueous solution of hydrochloride of condensation compounds of polyalkylenepolyamine and dicyandiamide for 10 to 30 minutes so that the condensation compounds form a hydrogen bond to a carboxyl group in the regenerated collagen fiber; and drying the immersed dyed regenerated collagen fiber at a predetermined temperature,
wherein the pH of the aqueous solution is in the range of 8.5 to 9.5 and the temperature there of is in the range of 55 to 65° C.
2. The method for fixing a dye in a dyed regenerated collagen fiber according to claim 1 , wherein
the dyed regenerated collagen fiber is a dyed fiber obtained by immersing a regenerated collagen fiber in a dye aqueous solution at 70° C. or lower.
3. The method for fixing a dye in a dyed regenerated collagen fiber according to claim 1 , wherein
the dyed regenerated collagen fiber is a dyed fiber obtained by immersing a regenerated collagen fiber in a dye aqueous solution in the range of pH 2 to 10.
4. A method for producing a dyed regenerated collagen fiber comprising:
a dyeing step of immersing a regenerated collagen fiber in an aqueous solution of least one kind of a dye selected from the group consisting of 1:1 type metal complex salt dyes, 1:2 type metal complex salt dyes and reactive dyes;
followed by a dye fixing step of immersing the dyed regenerated collagen fiber in an aqueous solution of hydrochloride of condensation compounds of polyalklenepolyamine and dicyandiamide for 10 to 30 minutes so that the condensation compounds form a hydrogen bond to a carboxyl group in the regenerated collagen fiber; and
a drying step of drying the immersed dyed regenerated collagen fiber at a predetermined temperature,
wherein the pH of the aqueous solution is in the range of 8.5 to 9.5 and the temperature thereof is in the range of 55 to 65° C. in the dye fixing step.
5. The method for producing a dyed regenerated collagen fiber according to claim 4 , wherein
the regenerated collagen fiber is immersed in the dye aqueous solution at 70° C. or lower in the dyeing step.
6. The method for producing a dyed regenerated collagen fiber according to claim 4 , wherein
the regenerated collagen fiber is immersed in the dye aqueous solution in the range of pH 2 to 10 in the dyeing step.