PVDF-based conductive composition
View Patent ↗The invention concerns a conductive composition comprising (by weight): 30 to 60 parts of a fluid PVDF; 25 to 62 parts of a viscous PVDF; 8 to 13 parts of a conductive filler; 0 to 2 parts of a fire retardant agent; 0 to 0.05 parts of a nucleating agent, based on a total of 100 parts. Preferably, it comprises by weight: 35 to 50 parts of a fluid PVDF; 45 to 55 parts of a viscous PVDF; 8 to 13 parts of a conductive filler; 0 to 2 parts of a fireproof agent; 0 to 0.05 parts of a nucleating agent, based on a total of 100 parts. Preferably, the conductive composition has a viscosity in the molten state at 230° C. of less than 10 6 Pa·s, preferably between 10 2 and 10 6 Pa·s. The invention also concerns multilayer structures combining the conductive composition and a thermoplastic polymer or a metal.
1. Conducting composition comprising, by weight
30 to 60 parts of a fluid thermoplastic polyvinylidene fluoride (PVDF) having a melt viscosity (measured at 230° C. and at 100 s −1 ) of between 4 and 15 kP;
25 to 62 parts of a viscous thermoplastic PVDF having a melt viscosity (measured at 230° C. and at 100 s −1 ) of between 15 and 40 kP;
8 to 13 parts of a conducting filler;
0 to 2 parts of a fire retardant; and
0 to 0.05 parts of a nucleating agent,
the total making 100 parts, wherein both said fluid thermoplastic PVDF and said viscous thermoplastic PVDF are a vinylidene fluoride homopolymer or vinylidene fluoride copolymer containing at least 75% by weight of VDF monomer units.
2. Composition according to claim 1 , comprising, by weight:
35 to 50 parts of fluid PVDF;
45 to 55 parts of viscous PVDF;
8 to 13 parts of a conducting filler;
0 to 2 parts of a fire retardant; and
0 to 0.05 parts of a nucleating agent,
the total making 100 parts.
3. Composition according to claim 1 , wherein the fluid PVDF is a homopolymer.
4. The conducting composition of claim 1 , wherein said melt viscosity for the fluid PVDF is between 4 and 10 kP.
5. Composition according to claim 1 , wherein the viscous PVDF is a copolymer.
6. Composition according to claim 5 , wherein the viscous PVDF is a VDF/HFP copolymer containing less than 10% hexafluoropropylene (HFP) by weight.
7. Composition according to claim 1 , wherein the conducting filler is a carbon black having a BET surface area of between 50 and 200 m 2 /g (ASTM D 3037-89) and a DBP (dibutyl phthalate) absorption of between 150 and 300 ml/100 g (ASTM D 2414-90).
8. Composition according to claim 7 , wherein the conducting filler is a carbon black having a BET surface area of between 50 and 100 m 2 /g and a DBP (dibutyl phthalate) absorption of between 150 and 250 ml/100 g.
9. Composition according to claim 1 , wherein the conducting filler has a volume resistivity (measured on a FINATHENE 47100 HDPE compound containing 25% carbon black by weight) of less than 20 Ω.cm.
10. Composition according to claim 1 , wherein the conducting composition has a melt viscosity at 230° C. of less than 10 6 Pa·s.