USE OF A HALOGEN-FREE FILM IN AN ADHESIVE MASKING TAPE, THE FILM BEING TEARABLE TRANSVERSELY AS A RESULT OF ELECTRON BEAM IRRADIATION
A masking tape for use preferably in the two-tone painting of plastic components for external mounting incorporates a halogen-free film composed of polyolefins, specifically a mixture composed of a polypropylene or a polypropylene copolymer and of a further polymer, selected from the group of the polyethylenes or ethylene copolymers, the film, before or after coating with the adhesive, being irradiated with electron beams, with a dose between 5 and 100 kGy (Kilograys), and the weight fraction of polypropylene or of polypropylene copolymer being at least 20%, based on the entirety of the polyolefins.
1 . A masking tape comprising a halogen-free film and an adhesive applied to one side of said film, the halogen-free film being composed of a mixture of polyolefins comprising a polypropylene or a polypropylene copolymer and comprising a further polymer, the further polymer being selected from the group of the polyethylenes or ethylene copolymers, the film, before or after application of the adhesive, being irradiated with electron beams, with a dose between 5 and 100 kGy (kilograys), and the weight fraction of polypropylene or of polypropylene copolymer being at least 20%, based on the entirety of the polyolefins.
2 . The masking tape as claimed in claim 1 , wherein the weight fraction of polypropylene or of polypropylene copolymer is at least 40%, based on the entirety of the polyolefins.
3 . The masking tape as claimed in claim 1 , wherein the polypropylene block copolymers are used as polypropylene component.
4 . The masking tape as claimed in claim 1 , wherein the further polymer is an ethylene-styrene copolymer or a copolymer of ethylene with polar comonomers.
5 . The masking tape as claimed in claim 1 , wherein the copolymers of ethylene are composed of ethylene and of a monomer component which is copolymerizable with ethylene.
6 . The masking tape as claimed claim 1 , wherein the polyolefins have an MFR of 0.5 to 15 g/10 min (190° C. and 2.16 kg in the case of polyethylenes, 230° C. and 2.16 kg in the case of polypropylenes).
7 . The masking tape claimed in claim 1 , which exhibits a breaking elongation of more than 100% (tensioning speed: 300 mm per minute, temperature: 23±1° C., relative humidity: 50±5%) and/or a tensile stress at 1% elongation of 1 to 10 N/cm.
8 . The masking tape as claimed in claim 1 , wherein the film is composed of two or more layers.
9 . The masking tape as claimed in claim 1 , wherein the film is unoriented.
10 . The masking tape as claimed in claim 1 , wherein the film is free of crosslinkers.
11 . A method of masking a substrate, which comprises applying a masking tape as claimed in claim 1 to said substrate.
12 . A method of painting a substrate, which comprises masking a portion of the substrate by applying a masking tape as claimed in claim 1 to said substrate, and thereafter painting another portion of said substrate to which said masking tape is not applied.