Low melt flow index resins for injections-stretch-blow-moulding

1. A method for preparing vials comprising:

providing a Ziegler-Natta formed random copolymer of propylene and from 2 to 3.5 wt. % ethylene exhibiting a melt index (MI 2 ) of from 1 to 3 dg/min., wherein an entirety of the random copolymer is prepared with a Ziegler-Natta catalyst; and

two-stage injection-stretch-blow-moulding the random copolymer to form a vial, wherein the two-stage injection-stretch-blow-moulding includes forming a perform at a preform injection temperature of at least 330° C. and a mould filling rate over gate diameter ratio that is at least 5 cc/s/mm; and wherein the two-stage-stretch-blow moulding comprises the following steps:

providing the preform by injection moulding on a multi-cavity mould;

cooling the preform to room temperature;

transporting the preform to the stretch-blow moulding machine;

re-heating the preform in the stretch-blow moulding machine;

optionally passing the heated preform through an equilibration zone to allow the heat to disperse evenly through the preform wall;

optionally, submitting the preform to a pre-blow step; and

stretching the preform axially by a centre rod and simultaneously orienting the preform radially by high pressure air, wherein a ratio of the centre rod diameter to the diameter of the preform is within 3% of 2/3.

2. The method of claim 1 ,

wherein the preform injection temperature is between 330° C. to 350° C. and the mould filling rate over gate diameter ratio is less than or equal to 10 cc/s/mm.

3. The method of claim 2 , wherein the melt index is of from 1.5 to 2.5 dg/min.

4. The method of claim 2 , wherein the perform is reheated in an infrared oven with an energy of from 28 to 40 kW for an output of 1500 bottles per hour.

5. The method of claim 2 , wherein the random copolymer exhibits a polydispersity index of at least 6.

6. The method of claim 2 , wherein the random copolymer comprises talc or sodium benzoate.

7. The method of claim 6 , wherein the talc or sodium benzoate is present in an amount up to 5000 ppm.

8. The method of claim 6 , wherein the talc or sodium benzoate is present in an amount ranging from 200 to 2500 ppm.

9. The method of claim 2 , wherein the random copolymer comprises no nucleating agent.

10. The method of claim 1 , wherein the perform is reheated in an infrared oven at a temperature of between 90 to 140° C.

11. The method of claim 1 , wherein the pre-blow pressure is from 4 to 6 bars.

12. The method of claim 1 , wherein stretching pressure is from 15 to 20 bars.

13. The method of claim 1 , wherein the stretch rod speed is between 1400 and 1800 mm/s.

14. The method of claim 1 , wherein the optional step of passing the heated preform through the equilibration zone to allow the heat to disperse evenly through the preform wall is performed.

15. The method of claim 1 , wherein the optional step of submitting the preform to the pre-blow step is performed.