Thermoplastic olefin polymer blend and adhesive films made therefrom

1. A multilayer film having at least 3 layers:

(A) an adhesive layer in an amount of from 5 to 25 volume percent consisting essentially of at least about 40 weight percent of an ethylene/alkyl acrylate copolymer having a Vicat point (ASTM D1525) of no more than 40° centigrade (° C.), at least about 1 and at most about 10 weight percent of an ethylene/α, β-ethylenically unsaturated carboxylic acid copolymer, and at least about 20 weight percent of a low density polyethylene, LDPE having a density of from about 0.91 to about 0.94 g/cm 3 , and 0 to at most about 7 weight percent filler, hereinafter referred to as composition A;

(B) a core layer, in an amount of 50 to 90 volume percent comprising at least about 20 weight percent linear low density polyethylene (LLDPE), at least about 20 weight percent low density polyethylene different from LLDPE, at least about 10 weight percent high density polyethylene and 0 to at most about 5 weight percent filler, hereinafter referred to as composition B and

(C) a melt barrier layer in an amount of from 5-25 volume percent, that is a layer that effectively prevents molten adhesive film layer polymer from migrating through the multilayer film surface to an external surface of the multilayer film consisting essentially of at least about 90 weight percent high density polyethylene, hereinafter referred to as composition C, with the remainder of the polymer being another polyolefin,

and in each layer, the percentages being based upon combined weight of polymers and filler and selected to total 100 percent by weight, wherein the multilayer film is strippable, that is removable, from a surface leaving little residue visible to the eye or sufficient to stick to other substances or interfere with further use.

2. The multilayer film of claim 1 wherein the alkyl acrylate is methyl acrylate and the copolymer has a methyl acrylate content of from 26 percent by weight to 31 percent by weight, based upon copolymer weight and wherein when the multilayer film is applied to an aluminum surface, the peel strength is sufficient to avoid unintentional or unassisted removal from the surface but not so high as to leave an adhesive residue when removed.

3. The multilayer film of claim 2 wherein the ethylene/α, β-ethylenically unsaturated carboxylic acid copolymer is an ethylene/acrylic acid copolymer that has an acrylic acid content within a range of from greater than or equal to 5 percent by weight to less than or equal to 22 percent by weight, based upon copolymer weight or an ethylene/methacrylic acid copolymer.

4. The multilayer film of claim 2 wherein the ethylene/α, β-ethylenically unsaturated carboxylic acid copolymer is an ethylene/methacrylic acid copolymer.

5. The multilayer film of claim 1 wherein the ethylene/α, β-ethylenically unsaturated carboxylic acid copolymer is an ethylene/acrylic acid copolymer that has an acrylic acid content within a range of from greater than or equal to 5 percent by weight to less than or equal to 22 percent by weight, based upon copolymer weight or an ethylene/methacrylic acid copolymer and wherein when the multilayer film is applied to an aluminum surface, the peel strength is sufficient to avoid unintentional or unassisted removal from the surface but not so high as to leave an adhesive residue when removed.

6. The multilayer film of claim 5 wherein the ethylene/α, β-ethylenically unsaturated carboxylic acid copolymer is an ethylene/methacrylic acid copolymer.

7. The multilayer film of claim 1 wherein the ethylene/α, β-ethylenically unsaturated carboxylic acid copolymer is an ethylene/methacrylic acid copolymer.

8. The multilayer film of claim 1 wherein Layer C comprises from 10 to 20 volume percent of the layers of the multilayer film.

9. The multilayer film of claim 1 wherein the film has at least 2 of the following properties:

an Ultimate Tensile Strength, MD from at least about 10 to at most about 30 N/mm 2 ;

an Ultimate Tensile Strength, TD from at least about 8 to at most about 25 N/mm 2 ;

an Ultimate Elongation, MD from at least about 250 to at most about 750 percent;

an Ultimate Elongation, TD from at least about 550 to at most about 1050 percent;

an Elmendorf Tear Strength, both MD and TD, independently from at least about 1 to at most about 25 g/μm;

a 2% Secant Modulus, both MD and TD independently from at least about 210 at most about 450 N/mm 2 ;

a Peel Strength from aluminum from at least about 0.40, more preferably to at most about 1.1 N per cm of width; and

a Hagerty Roughness from at least about 220 to at most about 700 mL/M.

10. The multilayer film of claim 1 wherein the film has a 230° Fahrenheit (110° centigrade) hot bar seal bond strength to a surface of aluminum foil, with a two second seal time that is greater than the 230° Fahrenheit (110° centigrade) hot bar seal bond strength of a multilayer film structure having the same melt barrier layer, and the same intermediate core layer, but with an adhesive layer that contains the same ethylene/methyl acrylate copolymer and is substantially free of the ethylene/acrylic acid copolymer.

11. The multilayer film of claim 1 wherein it is a part of a laminate further comprising at least solid material having a surface directly adhered to the multilayer film.

12. The multilayer film of claim 11 wherein the solid material comprises wood, wood product, or cementitious material, painted metal, plastic or a combination thereof.

13. A process of applying a multilayer film of claim 1 to at least one acrylic paint surface by lamination at a film temperature at or above 71.1° C.

14. The process of claim 13 wherein the multilayer film is applied to at least one painted wood surface, painted wood product surface, painted cementitious surface, painted metal surface, or plastic surface.