Method for preparing a latex from a chlorinated vinylic polymer
View Patent ↗Process for preparing a seed latex of a methyl methacrylate polymer (PMMA) by radical polymerization in aqueous emulsion of methyl methacrylate and optionally at least one comonomer. Process for preparing a chlorinated vinyl polymer latex by radical polymerization in aqueous emulsion of at least one chlorinated vinyl monomer, according to which the polymerization takes place in the presence of at most 3% by weight, expressed relative to the total weight of the monomers, of the PMMA seed latex.
1. A process for preparing a chlorinated vinyl polymer latex, the process comprising:
radically polymerizing at least one chlorinated vinyl monomer in an aqueous emulsion in the presence of a methyl methacrylate polymer seed latex,
wherein the polymerizing takes place in the presence of at most 3% by weight, expressed relative to a total weight of monomers, of dry matter of said methyl methacrylate polymer seed latex,
wherein particles of the methyl methacrylate polymer seed latex have an average diameter, measured by hydrodynamic fractionation, less than or equal to 60 nm, and
wherein a particle diameter distribution of the particles, determined by hydrodynamic fractionation, is monomodal and has a standard deviation less than or equal to 20 nm.
2. The process of claim 1 , wherein the polymerizing takes place in the presence of at most 1.5% by weight, expressed relative to the total weight of the monomers, of dry matter of the methyl methacrylate polymer seed latex.
3. The process of claim 1 , wherein a chlorinated vinyl polymer of the chlorinated vinyl polymer latex is a vinylidene chloride polymer.
4. The process of claim 1 , wherein the vinylidene chloride polymer is a copolymer of vinylidene chloride and at least one monomer selected from the group consisting of maleic anhydride, itaconic acid, methyl acrylate, methyl methacrylate, ethyl acrylate, ethyl methacrylate, n-butyl acrylate, n-butyl methacrylate, 2-ethylhexyl acrylate, 2-ethylhexyl methacrylate, 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate, glycidyl methacrylate, glycidyl acrylate, acrylonitrile, methacrylonitrile, acrylic acid, methacrylic acid, acrylamide, N-methylolacrylamide, 2-acrylamido-2-methylpropanesulphonic acid (AMPS) a salt of 2-acrylamido-2-methylpropanesulphonic acid, 2-sulphoethylmethacrylic acid (2-SEM) a salt of 2-sulphoethylmethacrylic acid, a phosphate ester of methacrylate-terminated polypropylene glycol salts, and a salt of a phosphate ester of methacrylate-terminated polypropylene glycol.
5. The process of claim 1 , wherein the particles of the methyl methacrylate polymer seed latex have an average diameter, measured by hydrodynamic fractionation, less than or equal to 40 nm.
6. The process of claim 1 , wherein the particles of the methyl methacrylate polymer seed latex have a monomodal particle diameter distribution, determined by hydrodynamic fractionation, with a standard deviation less than or equal to 10 nm.
7. The process of claim 1 , wherein the particles of the chlorinated vinyl polymer latex have an average diameter, measured by hydrodynamic fractionation, greater than or equal to 120 nm.
8. The process of claim 1 , wherein the particles of the chlorinated vinyl polymer latex have an average diameter, measured by hydrodynamic fractionation, of at most 200 nm.
9. The process of claim 1 , wherein the particles of the chlorinated vinyl polymer latex have a monomodal particle diameter distribution, determined by hydrodynamic fractionation.
10. The process of claim 1 , wherein the vinylidene chloride polymer comprises from 50 to 95% by weight of vinylidene chloride.