Nonaqueous electrolytic cell and its manufacturing method
View Patent ↗A nonaqueous electrolytic cell manufacturing method is characterized in that a nonaqueous electrolyte containing vinylene carbonate is used, a coating on the surface of the negative electrode is formed at the initial charging/discharging in such a way by lowering the negative electrode potential to less than 0.4 V with relative to the lithium potential, wherein the nonaqueous electrolytic cell comprises a nonaqueous electrolyte containing an electrolytic salt and a nonaqueous solvent, a positive electrode, and a negative electrode containing a negative electrode material into/from which lithium ions are inserted/desorbed at a potential higher than the lithium potential by 1.2 V. The nonaqueous electrolytic cell is used in a range of negative electrode potential nobler than the lithium potential by 0.8 V.
1. A method for manufacturing a nonaqueous electrolytic cell comprising a nonaqueous electrolyte containing an electrolyte salt and a nonaqueous solvent, a positive electrode, and a negative electrode containing a negative active material into/from which lithium ion is inserted/extracted at 1.2 V or higher potential than lithium potential, wherein a vinylene carbonate-containing nonaqueous electrolyte is used and at a time of initial charge-discharge, a negative electrode potential is lowered to less than 0.4 V relative to lithium potential to form a coat on the negative electrode surface.
2. The method for manufacturing a nonaqueous electrolytic cell according to claim 1 , wherein the negative electrode potential is lowered to less than 0.4 V relative to lithium potential by making a charge voltage at the time of initial charge-discharge higher than that in use.
3. The method for manufacturing a nonaqueous electrolytic cell according to claim 2 , wherein even in a region where the negative electrode potential is to less than 0.4 V relative to lithium potential, the positive electrode potential does not exceed 4.5 V to the lithium potential in an entire region where the negative electrode potential is to less than 0.4 V.
4. The method for manufacturing a nonaqueous electrolytic cell according to claim 1 ; wherein the nonaqueous electrolyte further containing 1,3-propane sultone is used at the time of initial charge-discharge.
5. The method for manufacturing a nonaqueous electrolytic cell according to claim 1 , wherein the nonaqueous solvent contains a cyclic carbonate other than vinylene carbonate and a linear carbonate.
6. The method for manufacturing a nonaqueous electrolytic cell according to claim 5 , wherein the cyclic carbonate is propylene carbonate and the linear carbonate is diethyl carbonate.
7. The method for manufacturing a nonaqueous electrolytic cell according to claim 1 , wherein a content of the vinylene carbonate is 10% by weight or less to that of the nonaqueous electrolyte.
8. The method for manufacturing a nonaqueous electrolytic cell according to claim 7 , wherein the content of the vinylene carbonate is 0.5 to 5% by weight to that of the nonaqueous electrolyte.
9. The method for manufacturing a nonaqueous electrolytic cell according to claim 1 , wherein a thickness of the coat of the negative electrode surface is 10 nm or more.
10. The method for manufacturing a nonaqueous electrolytic cell according to claim 1 , wherein the negative active material is a spinel type lithium titanate.
11. The method of using an electrolytic cell of claim 1 , comprising:
preparing a nonaqueous electrolytic cell comprising a nonaqueous electrolyte containing an electrolyte salt and a nonaqueous solvent, a positive electrode, and a negative electrode containing a negative active material into/from which lithium ion is inserted/extracted at 1.2 V or higher potential than lithium potential, wherein the nonaqueous electrolyte contains vinylene carbonate, and the negative electrode has a coat on a surface thereof, and
using the nonaqueous electrolytic cell in a range of a negative electrode potential nobler than lithium potential by 0.8 V.
12. The method of using the nonaqueous electrolytic cell according to claim 11 , wherein a positive active material is a lithium-transition metal composite oxide defined by a general formula LiMn x Ni y Co z O 2 (x+y+z=1; 0≦x≦0.5; 0≦y≦1; 0≦z≦1).
13. The method of using the nonaqueous electrolytic cell according to claim 11 , wherein a current collector of the negative electrode is of copper, nickel, or their alloy.
14. The method of using the nonaqueous electrolytic cell according to claim 11 , wherein in an internal gas in the nonaqueous electrolytic cell after the cell is left at 60° C. for 2 weeks, a ratio of a total volume of methane, ethylene, and ethane to a total volume of hydrogen, carbon dioxide, methane, ethylene, and ethane is less than 0.3%, and a ratio of a carbon dioxide volume to a cell capacity is less than 0.4 μl/mAh.