Manufacturing method of nitride phosphor or oxynitride phosphor
View Patent ↗To reduce impurity contents of carbon and oxygen not contributing to light emission, then suppress deterioration of emission intensity of a phosphor, and improve emission efficiency of this phosphor. Therefore, there is provided a firing method of nitride or oxynitride phosphors, wherein a crucible 11 made of nitride is used as a firing container, and firing is performed, with this crucible covered with a lid (container 10 ), to manufacture the phosphor. The phosphor is expressed by a general composition formula MABO o N 3-2/3O :Z in which element M is one or more kinds of elements having bivalent valency, element A is one or more kinds of elements having tervalent valency, element B is one or more kinds of elements having tetravalent valency, O is oxygen, N is nitrogen, and element Z is an activating agent, satisfying o≧0.
1. A method of manufacturing a nitride phosphor or an oxynitride phosphor, the method comprising:
placing raw material powders in a firing container made of boron nitride and covering the firing container with a lid made of boron nitride;
placing the firing container with the raw material powders therein in a firing furnace;
accommodating the firing container in a carbon container, such that the carbon container and the firing container with the raw material powders therein are located in the firing furnace;
vacuumizing an inside of the firing furnace and providing nitrogen atmosphere to the inside of the firing furnace; and
firing the raw material powders in a circulating nitrogen atmosphere,
wherein the phosphor is expressed by a general composition formula MABO o N 3-2/3o :Z in which element M is one or more different elements having bivalent valency, element A is one or more kinds of elements having tervalent valency, element B is one or more kinds of elements having tetravalent valency, O is oxygen, N is nitrogen, and element Z is an activating agent, satisfying o≧0, and
the phosphor contains less than 0.06 wt % of carbon.
2. The method according to claim 1 , wherein the element M is one or more different elements selected from a group consisting of Mg, Ca, Sr, Ba, Zn, the element A is one or more different elements selected from a group consisting of B (boron), Al, Ga, the element B is Si and/or Ge, and the element Z is one or more different elements selected from a group consisting of rare earth elements and transitional metal elements.
3. The method according to claim 1 , wherein the element A is Al, and the element B is Si.
4. The method according to claim 1 , wherein the element M is Ca, and the element Z is Eu.
5. The method according to claim 1 , wherein the lid is a container that is larger than the firing container and is turned upside down to cover at least an upper part of the firing container.
6. The method according to claim 1 , wherein the raw material powders are fired in a firing furnace having a carbon heater.
7. The method according to claims 1 , wherein the phosphor contains less than 2.7 wt % of oxygen.
8. A method according to claim 1 , wherein the phosphor contains indispensable oxygen.
9. A method according to claim 1 , wherein Z is Eu, and only Eu 2 O 3 (3N) is used as an Eu raw material.
10. A method according to claim 1 , wherein a molar ratio of raw materials Ca:Al:Si:Eu=0.985:1:1:0.015.