Laminated ballistic sheet
View Patent ↗A non-woven ballistic material that demonstrates exceptional ballistic properties which ballistic material is fabricated by the lamination or angular lamination of a plurality of wide sheets of UHMWPE comprising a plurality of strips of highly oriented ultra high molecular weight polyethylene partially overlapped or abutted longitudinally to define joints between adjoining strips wherein the thickness of the joint is less than about 80% of the thickness of the sum of the thicknesses of the adjoining strips that make up the joint.
1. A ballistic-resistant panel comprising a plurality of bonded, interleaved and angularly disposed layers of non-fibrous ultra high molecular weight polyethylene tape, said layers bonded together through the application of heat of at least 150 degrees F. and pressure of at least 150 psi;
each of said layers of non-fibrous ultra high molecular weight polyethylene tape comprising a plurality of tape strips of indeterminate length having a modulus of greater than 1,400 grams per denier and longitudinally joined together in a sheet structure;
said sheet structure includes partially overlapped or abutted strips of non-fibrous, ultra high molecular weight polyethylene tape that are bonded with heat and pressure to define joints between adjoining strips wherein said joints include a higher strength and higher modulus than the portions of the sheet outside the joints; and
said plurality of tape strips joined together by calendering an array of said overlapped or abutted strips at a temperature between 120° C. and 155° C. and at a pressure of at least 300 pounds per lineal inch (pli) and under a tension of between 0.3 grams/denier and 5 grams/denier.
2. The ballistic-resistant panel of claim 1 wherein the plurality of tape strips joined together in a sheet structure comprises partially overlapped or abutted strips of non-fibrous ultra high molecular weight polyethylene tape that define joints between adjoining strips wherein the thickness of the joints is no more than 80% of the sum of the thicknesses of the adjoining strips that make up the joint.
3. The ballistic resistant panel of claim 1 further including a single layer of adhesive between the layers of non-fibrous, ultra high molecular weight polyethylene tape.
4. The ballistic resistant panel of claim 3 wherein the adhesive is selected from the group consisting of: polyamide, ethylene vinyl acetate, polyurethane, ethylene acrylic acid, polyolefin and polystyrene isoprene copolymer adhesives.