A process is provided for the manufacture of polyvinyl alcohol, having an APHA color of equal to or less than about 10, by polymerizing a vinyl acetate monomer to form polyvinyl acetate and then hydrolyzing the polyvinyl acetate to form polyvinyl alcohol wherein the vinyl acetate monomer is characterized as having an inhibitor level of equal to or less than about 10 ppm, preferably less than about 5 ppm, more preferably less than about 3 ppm, even more preferably less than about 1 ppm.
1 . A process for the manufacture of polyvinyl alcohol having an APHA color of equal to or less than about 10, comprising polymerizing vinyl acetate monomer, having a level of inhibitor of about 10 ppm or less to form polyvinyl acetate and then hydrolyzing the polyvinyl acetate to form polyvinyl alcohol.
2 . The process of claim 1 , wherein the level of inhibitor is about 5 ppm or less.
3 . The process of claim 2 , wherein the level of inhibitor is about 3 ppm or less.
4 . The process of claim 3 wherein the level of inhibitor is about 1 ppm or less.
5 . A process for the manufacture of polyvinyl alcohol having an APHA color of equal to or less than about 10, comprising polymerizing vinyl acetate monomer, having a level of hydroquinone inhibitor of about 10 ppm or less, to form polyvinyl acetate and then hydrolyzing the polyvinyl acetate to form polyvinyl alcohol.
6 . The process of claim 5 wherein the level of hydroquinone is about 5 ppm or less.
7 . The process of claim 6 wherein the level of hydroquinone is about 3 ppm or less.
8 . The process of claim 7 wherein the level of hydroquinone is about 1 ppm or less.
9 . A process for the manufacture of laminated glass products, requiring low color, which comprises using a polyvinyl alcohol having an APHA color of less than or equal to about 10.
10 . The process of claim 9 wherein the intended application for the glass product is an automotive windshield.
11 . The process of claim 9 wherein the intended application for the glass product is selected from storm windows and doors.
12 . The process of claim 9 wherein the intended application for the glass product is ballistic windows.