Titanium production waste byproduct as partial cement replacement
View Patent ↗An industrial waste byproduct from a titanium metal or a titanium dioxide production process can be utilized as a partial cement replacement. In some embodiments, the byproduct can comprise a byproduct from the production of titanium dioxide pigment from a sulphate process or from a chloride process. The cement can be used to make concrete and other cementitious material products for structural and non-structural uses, for example, grout, mortar, gunite, stucco, masonry, decorative stonework, bricks, blocks, roof tiles, floor tiles, cobblestones, pavers, combinations thereof, and the like.
1. A cementitious material, consisting of:
water;
cement; and
a byproduct of at least one of a titanium metal and a titanium dioxide production process.
2. The cementitious material of claim 1 , wherein the byproduct is present in the cementitious material in an amount of at least about five percent by weight based on the total weight of the cementitious material.
3. The cementitious material of claim 1 , wherein the byproduct is present in the cementitious material in an amount of from about 10 percent by weight to about 30 percent by weight based on the total weight of the cementitious material.
4. The cementitious material of claim 1 , wherein the byproduct comprises a powder having an average specific surface area, as per ASTM C204, of from about 4000 cm 2 /g to about 4500 cm 2 /g.
5. The cementitious material of claim 1 , wherein the byproduct comprises a powder having an average specific gravity of from about 2.2 to about 2.4.
6. The cementitious material of claim 1 , wherein the byproduct comprises SiO 2 , Al 2 O 3 , Fe 2 O 3 , CaO, MgO, SO 3 , and MnO.
7. The cementitious material of claim 1 , wherein the byproduct has been produced via a chloride process for making titanium dioxide.
8. The cementitious material of claim 1 , wherein the cement is Portland cement.
9. A concrete mixture consisting of:
a cementitious material, the cementitious material consisting of cement and a byproduct of at least one of a titanium metal and a titanium dioxide production process;
aggregate; and
water.
10. The concrete mixture of claim 9 , wherein the cementitious material is present in an amount of from about 10 percent by weight to about 20 percent by weight based on the total weight of the concrete mixture.
11. The concrete mixture of claim 9 , wherein the ratio of the amount of the aggregate to the amount of the cementitious material is from about 0.5:1 to about 0.55:1, based on weight.
12. The concrete mixture of claim 9 , wherein the ratio of the water to the cementitious material is about 0.55:1, based on weight, and the concrete mixture exhibits an initial slump, as measured by test ASTM C143, of from about 65 mm to about 90 mm.