Method for producing polymer beads of uniform size
View Patent ↗A method for preparing monodisperse crosslinked bead polymers by introducing droplets having a harmonic mean size from 50 to 1500 microns and comprising at least one monomer, at least one crosslinker and a free-radical polymerization initiator into an aqueous medium through orifices to produce an aqueous suspension of droplets having a volume fraction of droplets from 35 to 64%; wherein the droplets are not encapsulated; causing the aqueous suspension of droplets to flow in a downward direction in a pipe in which the temperature is maintained at least 20° C. below the temperature at which the polymerization initiator has a half-life of 1 hour; and polymerizing the droplets in a reactor.
1. A method for preparing monodisperse crosslinked bead polymers comprising:
(a) introducing droplets having a harmonic mean size from 50 to 1500 microns and comprising at least one monomer, at least one crosslinker and a free-radical polymerization initiator into an aqueous medium through orifices to produce an aqueous suspension of droplets having a volume fraction of droplets from 35 to 64%; wherein the droplets are not encapsulated;
(b) causing the aqueous suspension of droplets to flow in a downward direction in a pipe such that: (i) a ratio of droplet harmonic mean size to inside pipe diameter is from 0.001 to 0.035; (ii) mean linear flow velocity is from 0.5 to 2.5 ft/s (0.15 to 0.75 m/s); and (iii) temperature is maintained at least 20° C. below a temperature at which the polymerization initiator has a half-life of 1 hour; and
(c) polymerizing the droplets in a reactor.
2. The method of claim 1 further comprising functionalizing the polymerized droplets as ion exchange resins.
3. The method of claim 1 in which the volume fraction of droplets is from 35% to 60%.
4. The method of claim 1 in which the harmonic mean size of the droplets is from 150 to 1000 microns.
5. The method of claim 4 in which the harmonic mean size of the droplets is from 150 to 500 microns; the ratio of droplet harmonic mean size to pipe diameter is from 0.002 to 0.022; and the mean linear flow velocity is from 0.5 to 1.8 ft/s (0.15 to 0.54 m/s).
6. The method of claim 5 in which in which the volume fraction of droplets is from 35% to 60%.
7. The method of claim 4 in which the harmonic mean size of the droplets is from 450 to 900 microns; the ratio of droplet harmonic mean size to pipe diameter is from 0.008 to 0.032; and the mean linear flow velocity is from 0.9 to 2.5 ft/s (0.27 to 0.75 m/s).
8. The method of claim 7 in which in which the volume fraction of droplets is from 35% to 60%.
9. The method of claim 1 in which the harmonic mean size of the droplets is from 150 to 900 microns; the ratio of droplet harmonic mean size to pipe diameter is from 0.002 to 0.032; the mean linear flow velocity is from 0.5 to 1.9 ft/s (0.15 to 0.57 m/s); the volume fraction of droplets is from 35% to 55%; and the droplets polymerize to form a styrenic polymer.
10. The method of claim 9 further comprising functionalizing the polymerized droplets as ion exchange resins.