Method for coating silicone hydrogels
View Patent ↗The invention relates to a process for producing biomedical articles, in particular, silicone hydrogel contact lenses having durable hydrophilic chitosan coating. The chitosan coating is covalently attached to the medical device by performing a crosslinking reaction between chitosan and the carboxylic groups on the surface of a medical device directly in a sealed package during autoclave. The coated biomedical articles obtainable by the process of the invention have desirable characteristics regarding adherence to the substrate, durability, hydrophilicity, wettability, biocompatibility and permeability and are thus especially useful in the field of ophthalmic devices.
1. A process for coating a medical article comprises the steps of:
(a) providing an uncoated medical article, wherein the article comprises a hydrophobic bulk material made of a silicone hydrogel containing carboxylic acid groups;
(b) contacting the medical article with a C 2 -C 4 alcohol for a predetermined period of time;
(c) contacting the medical article treated in step (b) with a solution comprising chitosan to form a non-covalently attached coating of chitosan on the medical article;
(d) contacting the medical article with the chitosan coating in a lens package containing a packaging solution comprising a crosslinking agent selected from the group consisting of aliphatic C 2 -C 10 -dialdehydes, formaldehyde and genipin; and
(e) autoclaving said package with the medical article and the packing solution therein, wherein the chitosan coating the medical article is covalently attached through the crosslinking agent to the carboxylic acid groups on the medical article surface, wherein the resultant medical article has a hydrophilicity characterized by an average water contact angle of about 80 degrees or less.
2. A process of claim 1 , wherein the step (b) is performed at a temperature of from 15° C. to 75° C. for a time period of ≦5 minutes, wherein the C 2 -C 4 alcohol is selected from the group consisting of ethanol, 1-propanol and 2-propanol, wherein the chitosan solution has a pH value in the range of 5.8-6.3, wherein the crosslinking agent is selected from the group consisting of glutardialdehyde, formaldehyde and genipin.
3. A process according to claim 2 , wherein the medical article is a soft contact lens.
4. A process according to claim 3 , wherein the silicone hydrogel comprises copolymerized acrylic acid moieties.
5. A process according to claim 4 , wherein the crosslinking agent is glutardialdehyde.
6. A process according to claim 5 , wherein the article is contacted with 2-propanol at a temperature of from 60° C. to 75° C. over a time period of 1 minute.
7. A process according to claim 3 , wherein the crosslinking agent is formaldehyde.
8. A process according to claim 6 , wherein the article is contacted with ethanol at a temperature of from 15° C. to 30° C. over a time period of ≦1 minute.
9. A process according to claim 3 , wherein the crosslinking agent is genipin.