Crosslinked polymeric material with enhanced strength and process for manufacturing
View Patent ↗A radiation crosslinked (50 kGy), pressure-treated UHMWPE material has been developed by applying compressive force on a crosslinked polymer in a direction orthogonal to an axial direction. The deformed material is then cooled while held in a deformed state. The resulting material is anisotropic, with enhanced strength oriented along the axial direction. The directionally engineered material is oxidatively stable even after four weeks of accelerated aging in a pressure vessel containing five atmospheres of oxygen (ASTM F2003). Because of its oxidative stability, the deformation processed material is a suitable candidate for air-permeable packaging and gas sterilization, which has thus far been reserved for remelted highly crosslinked UHMWPEs.
1. A method for treating a polymeric bulk material comprising
heating a bulk material comprising a cross-linked polymer to a compression deformable temperature, the polymer being in an elongated bulk form characterized by an axial direction in the direction of the elongation;
applying force to deform the heated bulk material in a direction orthogonal to the axial direction;
cooling the bulk material to a solidification temperature while maintaining the polymer in a deformed state; and
stress relieving the cooled bulk material by heating it to a stress relief temperature, wherein the bulk material is held straight in the axial direction in a mechanical device during the stress relieving.
2. A method according to claim 1 , wherein the compression deformable temperature is less than the melting point of the polymer and greater than the melting point minus 50° C.
3. A method according to claim 1 , wherein the bulk material is in the form of a cylindrical rod.
4. A method according to claim 1 , wherein applying force comprises reducing a dimension of the bulk material in the orthogonal direction.
5. A method according to claim 1 , comprising extruding the heated bulk material through a reducing die.
6. A method according to claim 1 , wherein the polymer is crosslinked with gamma-irradiation.
7. A method according to claim 1 , wherein the polymer is ultrahigh molecular weight polyethylene (UHMWPE).
8. A method according to claim 7 , wherein the compression deformable temperature is less than the melting point and greater than the melting point minus 50° C.
9. A method according to claim 7 , wherein the UHMWPE is in the form of a cylindrical rod.
10. A method according to claim 7 , wherein the UHMWPE is crosslinked with gamma-irradiation.
11. A method according to claim 7 , wherein the UHMWPE is crosslinked with from 0.01 to 10 Mrad of gamma-irradiation.
12. A method according to claim 7 , comprising extruding the heated UHMWPE through a reducing die.
13. A method according to claim 7 , comprising cooling the deformed polymer to a temperature below 30° C. to solidify it.
14. A method according to claim 7 , wherein the stress relieving temperature is above about 100° C. and below the melting point of the UHMWPE.
15. A method according to claim 14 , wherein stress relieving is carried out at 125-135° C.
16. A method for making an implant bearing component, comprising machining the component from a UHMWPE prepared according to claim 14 .
17. An implant, comprising UHMWPE prepared according to claim 14 .
18. A method for treating crosslinked UHMWPE to make material suitable for use in medical implants comprising
heating UHMWPE to a temperature above about 80° C. and below its melting point, wherein the UHMWPE has been crosslinked with gamma-irradiation and is in the form of a bulk material characterized by an axial direction, a transverse direction orthogonal to the axial direction and an original transverse dimension;
applying compressive force to reduce a dimension of the bulk material in the transverse direction;
cooling the bulk UHMWPE to a solidification temperature while maintaining compressive force sufficient to prevent the bulk material from returning to its original transverse dimension, and
after cooling, annealing by heating at a stress relief temperature below the melting point of the UHMWPE to permit the transverse dimension to return to a dimension closer to its original value, wherein the bulk material is held in a mechanical device during the annealing to keep the material straight in the axial direction.
19. A method according to claim 18 , wherein applying compressive force comprises extruding the bulk material through a reducing die.
20. A method according to claim 18 , comprising extruding the heated crosslinked bulk material through a reducing die into a chamber dimensioned to hold the bulk material at a dimension in the transverse direction less than its original transverse dimension.
21. A method according to claim 18 , comprising heating the bulk crosslinked UHMWPE to a temperature greater than 100° C., extruding through a reducing die, and cooling the extruded UHMWPE to below 30° C. in a cooling chamber.
22. A method according to claim 18 , comprising heating the bulk UHMWPE to about 130° C., extruding the heated UHMWPE through a reducing die into a cooling chamber, and holding the extruded bulk material in the cooling chamber until the temperature of the cooling chamber drops to 30° C.
23. A method according to claim 18 , wherein the stress relief temperature is above 100° C.
24. A method according to claim 18 , wherein the mechanical device comprises V-channels.
25. A method according to claim 23 , wherein the stress relief heating is at 120° C. or higher.
26. A method according to claim 23 , wherein the stress relief heating is at about 125° C. to 135° C.
27. An implant, comprising UHMWPE treated according to claim 23 .
28. A method of making a bearing component made of UHMWPE, suitable for use in a medical implant, comprising:
radiation crosslinking a UHMWPE;
preheating the crosslinked UHMWPE to a temperature above 80° C. and below its melting point;
solid state extruding the UHMWPE at a draw ratio of greater than 1;
cooling the extruded UHMWPE to a solidification temperature below 80° C. while maintaining diametral compression;
annealing the cooled UHMWPE at a temperature below the melting point for a time sufficient for the rod to increase in diameter in response to the annealing while holding the rod straight in a mechanical device during the annealing; and
machining the component from the annealed UHMWPE.
29. A method according to claim 28 , comprising crosslinking to a dose of 0.01 to 10 MRad, heating to a compression deformable temperature of 125-135° C., extruding with a draw ration of 1.2 to 1.8, cooling to a solidification temperature of 30° C., and stress relieving at 125-135° C.
30. An implant comprising a bearing component made by a process according to claim 28 .
31. An implant comprising a bearing component made by a process according to claim 29 .