EXTRUDED POLYMER FOAMS CONTAINING BROMINATED 2-OXO-1,3,2-DIOXAPHOSPHORINANE COMPOUNDS AS FLAME RETARDANT ADDITIVES
Extruded polymer foams are prepared using 5,5-bis(bromomethyl)-2-oxo-1,3,2-dioxaphosphorinane or brominated 2-oxo-1,3,2-dioxaphosphorinane compounds. The brominated FR additives unexpectedly are stable at the extrusion temperatures, and provide excellent flame retardancy to the foams.
1 . A process comprising forming a pressurized mixture of (A) a molten styrene homopolymer or copolymer, a flame retarding amount of (B) or (B1) or a mixture of (B) and (B1), wherein (B) is at least one 5,5-bis(bromomethyl)-2-oxo-1,3,2-dioxaphosphorinane compound and (B1) is at least one alkane or cycloalkane that is substituted with (1) at least one 2-oxo-1,3,2-dioxaphosphorinane group and (2) at least one bromine atom, and (C) a blowing agent, and extruding the mixture into a region of reduced pressure such that the mixture expands and cools to form an expanded polymer containing component (B), (B1) or both (B) and (B1).
2 . The process of claim 1 , wherein wherein the pressurized, molten mixture is brought to a temperature of at least 180° C. prior to extruding the mixture.
3 . The process of claim 2 , wherein the pressurized, molten mixture is brought to a temperature of at least 190° C. prior to extruding the mixture.
4 . The process of claim 3 , wherein the pressurized, molten mixture is brought to a temperature of at least 200° C. prior to extruding the mixture.
5 . The process of claim 4 , wherein the 5,5-bis(bromomethyl)-2-oxo-1,3,2-dioxaphosphorinane compound is present and has the structure:
wherein T is a covalent bond, oxygen, sulfur or —NR 1 —, wherein R 1 is hydrogen, alkyl or inertly substituted alkyl, n is at least 1, and R is an unsubstituted or inertly substituted organic group that is bonded to the -T- linkage through a carbon atom on the R group.
6 . The process of claim 4 , wherein the 5,5-bis(bromomethyl)-2-oxo-1,3,2-dioxaphosphorinane compound is present and has any of the structures:
7 . The process of claim 4 , wherein component B1 is present and has the structure:
wherein T is a covalent bond, oxygen, sulfur or —NR 1 —, and A represents an alkane or cycloalkane group that is substituted with at least one bromine atom and is bonded to the -T- linkage through a carbon atom on the A group.
8 . The process of claim 4 , wherein component B1 is present and has any of the structures:
9 . The process of claim 4 , wherein the pressurized mixture further contains a melt flow promoter.
10 . The process of claim 4 , wherein the blowing agent includes water, carbon dioxide, or both water and carbon dioxide.
11 . An extruded combustible styrene homopolymer or copolymer foam, having a density of from 1 to about 30 lb/ft 3 (16-480 kg/m 3 ) and containing at least one 5,5-bis(bromomethyl)-2-oxo-1,3,2-dioxaphosphorinane compound, at least one alkane or cycloalkane that is substituted with at least one 2-oxo-1,3,2-dioxaphosphorinane group and at least one bromine atom, or a mixture thereof.