Highly flame retardant panels
View Patent ↗A flame retardant panel structure comprises at least one external metal layer, one or more tie layers comprising one or more functionalized polymers, and a core layer made of a fabric made of glass fibers. The flame retardant panel structure shows comparable flame retardancy properties while being manufactured at reasonable costs with conventional processes such as for example extrusion or calendering. The flame retardant panel structures can be used in applications where flame retardancy and/or fire protection is needed, such as for example in building and construction applications, automotive or railways applications, medical equipments and luggage.
1. A flame retardant panel structure comprising, in the order:
(i) at least one external metal layer;
(ii) one or more tie layers comprising one or more functionalized polymers; and
(iii) a core layer made of a fabric of glass fibers.
2. The structure according to claim 1 wherein
the structure comprises, in the order, (i) one external metal layer; (ii) one or more tie layers comprising one or more functionalized polymers; (iii) a core layer made of a fabric of glass fibers; and (iv) one or more additional tie layers comprising the functionalized polymer;
the functionalized polymer is independently selected from the group consisting of (a) anhydride functionalized polymer, (b) ethylene acid copolymer, (c) copolymer comprising copolymerized units of ethylene and a comonomer, or mixtures of two or more of (a), (b), and (c); and
the comonomer is C 4 -C 8 unsaturated anhydride, monoester of C 4 -C 8 unsaturated acids having at least two carboxylic acid groups, diester of C 4 -C 8 unsaturated acids having at least two carboxylic acid groups, or mixtures of two or more thereof.
3. The structure according to claim 2 wherein the structure further comprises (v) one additional external metal layer and the tie layer or the additional tie layer has a thickness between 10 and 500 μm.
4. The structure according to claim 3 wherein the functionalized polymer is the anhydride-grafted polymer and the polymer of the anhydride-grafted polymer is polyethylene, polypropylene, ethylene vinyl acetate, ethylene methyl (meth)acrylate, ethylene ethyl (meth)acrylate, ethylene butyl (meth)acrylate, or mixtures of two or more thereof.
5. The structure according to claim 4 wherein the anhydride-grafted polymer is grafted with about 0.01 to about 3 wt-% of an unsaturated dicarboxylic acid anhydride, the weight % being based on the total weight of the anhydride-grafted polymer.
6. The structure according to claim 2 wherein the functionalized polymer is the ethylene acid copolymer and is ethylene acrylic acid copolymer, ethylene methacrylic acid copolymer, ethylene maleic acid monoethylester copolymer, or mixtures of two or more thereof
7. The structure according to claim 6 wherein the ethylene acid copolymer comprises from about 1 to about 30 wt-% of an α,β-unsaturated C 3 -C 8 carboxylic acid, the weight % being based of the total weight of the ethylene acid copolymer.
8. The structure according to claim 5 wherein the core layer has a thickness between 2 and 5 mm.
9. The structure according to claim 8 wherein each of the external metal layer and the additional metal layer is independently aluminum, stainless steel, copper, steel, brass, or alloys of two or more thereof.
10. The structure according to claim 9 wherein the external metal layer is aluminum.
11. The structure according to claim 9 the additional metal layer is aluminum.
12. The structure according to claim 11 wherein the tie layer or the additional tie layer further comprises a non-reactive inorganic filler.
13. The structure according to claim 7 wherein the tie layer or the additional tie layer further comprises a non-reactive inorganic filler and the ore layer has a thickness between 2 and 5 mm.
14. The structure according to claim 12 wherein the fabric of glass fiber is impregnated with a phenolic resin.
15. The structure according to claim 13 wherein the fabric of glass fiber is impregnated with a phenolic resin.
16. The structure according to claim 12 further comprising one or more additional layers between the core layer and the tie layer.
17. The structure according to claim 16 wherein the additional layer comprises a flame retardant composition.
18. The structure according to claim 2 further comprising an outside layer that is adjacent to the external metal layer, which outside layer is made of an ionomeric composition.
19. The structure according to claim 18 wherein the tie layer or the additional tie layer is independently grafted polyethylene, grafted polypropylene, grafted ethylene vinyl acetate copolymer, grafted ethylene alkyl (meth)acrylate copolymer, or mixtures of two or more thereof.
20. The structure according to claim 12 further comprising a base substrate which is building panel, construction panel, automotive part, railway part, or medical equipment.