Positive electrode materials for high discharge capacity lithium ion batteries
View Patent ↗Positive electrode active materials are described that have a high tap density and high specific discharge capacity upon cycling at room temperature and at a moderate discharge rate. Some materials of interest have the formula Li 1+x Ni α Mn β Co γ O 2 , where x ranges from about 0.05 to about 0.25, α ranges from about 0.1 to about 0.4, β ranges from about 0.4 to about 0.65, and γ ranges from about 0.05 to about 0.3. The materials can be coated with a metal fluoride to improve the performance of the materials especially upon cycling. Also, the coated materials can exhibit a very significant decrease in the irreversible capacity lose upon the first charge and discharge of the battery.
1. A positive electrode active material for a lithium ion battery,
having a 10 th cycle specific discharge capacity of at least 250 mAh/g at room temperature, a tap density of at least 1.8 g/mL, and substantially spherically shaped particles with substantially uniform size, wherein the specific discharge capacity is determined at a discharge rate of C/3 when discharged from 4.6 volts to 2.0 volts after the material is activated in the first cycle through a charge to 4.6V at a rate of C/10; and
comprising a composition having an x-ray diffractogram characteristic of a rock-salt type structure and a formula Li 1+x Ni α Mn β Co γ M″ δ O 2−z F z , where x ranges from about 0.05 to about 0.25, α ranges from about 0.1 to about 0.4, β ranges from about 0.4 to about 0.65, γ ranges from about 0.05 to about 0.3, δ ranges from about 0 to about 0.1 and z ranges from about 0 to about 0.1, and where M″ is Mg, Zn, Al, Ga, B, Zr, Ti, Ca, Ce, Y, Nb or combinations thereof.
2. The positive electrode active material of claim 1 wherein the material comprises from about 0.1 mole percent to about 4 mole percent metal fluoride as a coating.
3. The positive electrode active material of claim 2 wherein the metal fluoride comprises AlF 3 .
4. The positive electrode active material of claim 1 wherein the material has a 10th cycle discharge capacity from about 250 mAh/g to about 310 mAh/g at room temperature at a discharge rate of C/3 when discharged from 4.6 volts to 2.0 volts.
5. The positive electrode active material of claim 1 having a tap density of at least 2.0 g/mL.
6. A secondary lithium ion battery comprising a positive electrode comprising the positive electrode active material of claim 1 , a negative electrode comprising a lithium intercalation composition and a separator between the positive electrode and the negative electrode.
7. The positive electrode active material of claim 1 wherein the material has a 20th cycle discharge capacity that is at least about 98.5% of the 5th cycle discharge capacity when discharged at room temperature at a discharge rate of C/3.
8. The positive electrode active material of claim 1 having a 10 th cycle specific discharge capacity of at least 260 mAh/g at room temperature, wherein the specific discharge capacity is determined at a discharge rate of C/3 when discharged from 4.6 volts to 2.0 volts.
9. The positive electrode active material of claim 1 wherein the positive electrode active material comprises a suitable coating to provide cycling enhancement.
10. The positive electrode active material of claim 9 wherein the first cycle irreversible capacity loss of the positive electrode active material is no more than about 2/3 of the first cycle irreversible capacity loss of the uncoated positive electrode active material, both cycled at discharge rate of C/10.
11. The positive electrode active material of claim 9 wherein the coating comprises Al 2 O 3 .