Methods and compositions for acid treatment of a metal surface
View Patent ↗The invention relates to compositions and methods that are useful in etching a metal surface. In particular, the invention relates to novel acid compositions and methods of using such compositions in etching a metal surface, preferably an aluminum surface prior to anodizing to dissolve impurities, imperfections, scale, and oxide. The compositions are effective in maintaining their etching capacity and in removing smut produced by the etching of a surface as well as in general cleaning.
1. A method of etching aluminum, said method comprising contacting said aluminum with a composition consisting essentially of:
(a) about 20 to about 80 grams per liter of ammonium bifluoride;
(b) about 1 to about 50 grams per liter of diammonium phosphate;
(c) a surfactant; and
(d) water.
2. The method of claim 1 , wherein said etching is performed at a pH of about 2 to about 5.
3. The method of claim 1 , further comprising rinsing the etched aluminum.
4. The method of claim 1 , wherein said composition comprises about 1 to about 3 g/L of said surfactant.
5. The method of claim 1 , wherein said aluminum is an aluminum alloy.
6. The method of claim 1 , wherein the etched aluminum is resistant to pitting.
7. The method of claim 1 , wherein the etch aluminum bath does not require cooling.
8. The method of claim 1 , wherein the etched aluminum is analyzed using a reflectometer at a 60° angle and has a uniform matte finish.
9. The method according to claim 1 , wherein extrusion lines on said etched aluminum are removed or minimized.
10. The method of claim 1 , which results in a significant reduction of waste products from the aluminum etching process.
11. The method of claim 1 , wherein said etching removes about 0.5 to about 1.5 gr/ft 2 of aluminum.
12. The method of claim 1 , which results in a reduction of water consumption in the aluminum etching process.
13. The method according to claim 1 , wherein said etching is performed at a composition temperature of 70° F. to 150° F.
14. The method of claim 13 , wherein said etching is performed at a temperature of about 100° F. to about 125° F.
15. The method according to claim 1 , wherein said etching is performed in about 0.5 to about 10 minutes.
16. The method of claim 15 , wherein said etching is performed in about 1 to about 3 minutes.
17. A method of etching aluminum, said method comprising etching said aluminum with a composition comprising hydrofluoric acid, fluoroboric acid, ammonium bifluoride, sodium phosphate, and a surfactant.
18. The method of claim 17 , wherein said composition further comprises water.