Bituminous mixtures comprising thermoplastic polymer membranes

1. A bituminous mixture comprising:

i. from 2 to 8 wt % of bitumen (A);

ii. from 27 to 98 wt % of mineral aggregates (B); and

iii. from 0 to 65 wt % of (C), (D), or a mixture of (C) and (D), wherein (C) represents one or more inorganic fillers and (D) represents mineral aggregates that are different from mineral aggregates (B) and that have a particle size of less than 4 mm (D),

wherein the mineral aggregates (B) are substantially completely coated with a thermoplastic polymer composition, and said thermoplastic polymer composition comprises PVB,

wherein, when present, the inorganic fillers (C) or the mineral aggregates (D) are uncoated, partially coated or substantially completely coated with the thermoplastic polymer composition, and

wherein the weight percentages are based on the total weight of the bituminous mixture.

2. The bituminous mixture according claim 1 , wherein the mineral aggregates (B) have a particle size of at least 2 mm.

3. The bituminous mixture according to claim 2 , wherein the mineral aggregates (B) have a particle size of at least 4 mm.

4. The bituminous mixture according to claim 1 , wherein the average thickness of the thermoplastic polymer coating on the mineral aggregates (B) is smaller than 1600 μm.

5. The bituminous mixture according to claim 4 , wherein the average thickness of the thermoplastic polymer coating on the mineral aggregates (B) is between 2 and 200 μm.

6. The bituminous mixture according to claim 1 , wherein the amount of the one or more inorganic fillers (C) is a non-zero amount up to 15 wt %.

7. The bituminous mixture according to claim 1 , wherein the mineral aggregates having a particle size of less than 4 mm (D) is a non-zero amount up to 50 wt %.

8. The bituminous mixture according to claim 1 further comprising fibers.

9. The bituminous mixture according to any preceding claim, wherein the thermoplastic polymer composition further comprises one or more materials selected from the group consisting of polyolefin, polyamide, polyester, and polyvinylacetate.

10. The bituminous mixture according to claim 1 , wherein the thermoplastic polymer composition comprises a recovered or recycled thermoplastic polymer.

11. The bituminous mixture according to claim 10 , wherein the thermoplastic polymer composition that coats mineral aggregates (B) comprises recovered or recycled PVB obtained from laminated glass.

12. A process for preparing the bituminous mixtures of claim 1 , comprising the steps of:

a) mixing and heating the mineral aggregates (B) at a temperature between 120 and 240° C.;

b) adding the thermoplastic polymer composition to the mineral aggregates obtained under (a) and stirring to obtain a uniformly coated mineral aggregate (B),

c) after the step b), a step of adding one or more inorganic fillers (C), mineral aggregates having a particle size of less than 4 mm (D), fibers or any combination of two or more of (C), (D) and the fibers to the mixture obtained under b) and stirring to obtain a substantially uniform mixture, and

d) adding the bitumen (A) to the mixture obtained under b) and stirring to obtain the bituminous mixture.

13. The process according to claim 12 , wherein the thermoplastic polymer composition added under step b) has the physical form of flakes.

14. The process according to claim 13 , wherein the flakes have a size less than 100 mm.

15. The process according to claim 14 , wherein the flakes have a size less than 5 mm.

16. The process according to claim 13 , wherein the flakes have a specific surface area larger than 10 cm 2 /g.