Moisture resistant polyimide compositions
View Patent ↗The invention relates to a moisture resistant composition comprising: a) from 20 to 80 weight percent based on the total weight of the composition of a polyetherimide copolymer made from a monomer mixture comprising 3,3′ bisphenol-A dianhydride (BPADA), and 4,4′-diaminodiphenyl sulfone (DDS); b) from 5 to 75 weight percent based on the total weight of the composition of polyetheretherketone (PEEK); and c) from 0 to 30 weight percent based on the total weight of the composition of a filler. The invention relates to a reflector substrate comprising a moisture resistant layer metalized with a reflective layer, wherein the moisture resistant layer comprising the moisture resistant composition. The invention relates to a method for producing a metalized coating without a primer comprising applying a reflective layer directly to a moisture resistant layer in the absence of a primer, wherein the moisture resistant layer comprises the moisture resistant composition.
1. A moisture resistant composition comprising a polymeric component consisting essentially of:
a) 25 weight percent, based on the total weight of the composition, of a polyetherimide copolymer made from a monomer mixture comprising 3,3′ bisphenol-A dianhydride (BPADA), and 4,4′-diaminodiphenyl sulfone (DDS); and
b) 66 weight percent, based on the total weight of the composition, of polyetheretherketone (PEEK);
the moisture resistant composition further comprising
c) 9 weight percent, based on the total weight of the composition, of a silica filler;
wherein, in conditions of dry atmosphere/260° C. and 60° C./60% relative humidity, articles having thicknesses of 2-3 mm, molded from the moisture resistant composition, each exhibit no popcorning and a warpage of less than or equal to 0.5 mm.
2. The moisture resistant composition of claim 1 , wherein the monomer mixture further comprises 3-chlorophthalic anhydride.
3. The moisture resistant composition of claim 1 , wherein a molded part comprising the moisture resistant composition of claim 1 , and having a thickness of 3 mm does not exhibit warping in a dry atmosphere at 260° C.
4. The moisture resistant composition of claim 1 , wherein a molded part comprising the moisture resistant composition of claim 1 , and having a thickness of 3 mm does not exhibit warping at 60° C./60% relative humidity.
5. The moisture resistant composition of claim 1 , wherein the polyetherimide copolymer of component a) is made from a monomer mixture consisting of 3,3′ bisphenol-A dianhydride (BPADA), and 4,4′-diaminodiphenyl sulfone (DDS).