Composition for high performance glass fibers and fibers formed therewith
View Patent ↗A composition for the manufacture of high strength glass fibers suitable for manufacture in a refractory lined glass melter is disclosed. The glass composition of the present invention includes 64-75 weight % SiO 2 , 16-24 weight % Al 2 O 3 , 8-11 weight % MgO and 0.25 to 3.0 weight % R 2 O where R 2 O is the sum of Li 2 O and Na 2 O. A composition of the present invention includes 64-75 weight % SiO 2 , 16-24 weight % Al 2 O 3 , 8-11 weight % MgO and 0.25 to 3.0 weight % Li 2 O. Another composition includes 68-69 weight percent SiO 2 , 20-22 weight percent Al 2 O 3 , 9-10 weight percent MgO and 1-3 weight percent Li 2 O. By using oxide based refractory lined furnaces the cost of production of glass fibers is substantially reduced in comparison with the cost of fibers using a platinum lined melting furnace. Fibers formed by the present invention are also disclosed. The fibers have a fiberizing temperature of less than 2650° F., a ΔT of at least 80° F. Further, the glass fibers have a strength in excess of 680 KPSI, in some instances a strength in excess of about 700 KPSI, and in others a strength in excess of about 730 KPSI. The glass fibers will desirably have a modulus greater than 12.0 MPSI, in some instances greater than about 12.18 MPSI, and in certain instances greater than about 12.7 MPSI.
1. A composition for high strength glass fibers comprising:
64-75 weight percent SiO 2 ;
16-24 weight percent Al 2 O 3 ;
8-11 weight percent MgO;
0.25-3 weight percent Li 2 O; and
no more than 1.0 weight percent of CaO impurities, wherein said glass fibers produced from said composition have a fiberizing temperature of less than about 2650° F. and a strength of greater than about 700 KPsi.
2. The composition of claim 1 , wherein the composition further comprises less than 5 weight percent total of one or more compounds selected from the group consisting of P 2 O 5 , ZnO, ZrO 2 , SrO, BaO, SO 3 , F 2 , B 2 O 3 , TiO 2 and Fe 2 O 3 .
3. The composition of claim 1 , wherein glass fibers produced from said composition have a ΔT of at least 80° F.
4. The composition of claim 1 , wherein:
said Al 2 O 3 is present in said composition in an amount from about 17 to about 22 weight percent;
said MgO is present in said composition in an amount from about 9 to about 11 weight percent; and
said Li 2 O is present in said composition in an amount from about 1.75 to 3.0 weight percent.
5. The composition of claim 1 , wherein the components of said composition are meltable in a refractory-lined melter.
6. A high strength glass fiber formed from a composition comprising:
64-75 weight percent SiO 2 ;
16-24 weight percent Al 2 O 3 ;
8-11 weight percent MgO;
0.25-3 weight percent Li 2 O, and
no more than 1.0 weight percent of CaO impurities, wherein said glass fiber has a fiberizing temperature of less than about 2650° F. and a strength of greater than about 700 KPsi.
7. The high strength glass fiber of claim 6 , wherein the fiber has a modulus greater than about 12.0 MPsi.
8. The high strength glass fiber of claim 6 , wherein said fiber has a pristine fiber tensile strength greater than about 730 KPsi.
9. The high strength glass fiber of claim 6 , wherein said fiber has a fiberizing temperature less than about 2600° F.
10. The high strength glass fiber of claim 9 , wherein said fiber has a liquidus temperature that is at least 80° F. below said fiberizing temperature.
11. The high strength glass fiber of claim 6 , wherein said fiber has a ΔT of at least 80° F.
12. The high strength glass fiber of claim 6 , wherein said fiber has a liquidus temperature that at least 80° F. below the fiberizing temperature.
13. The composition of claim 6 , wherein Li 2 O is present in said composition in an amount from about 1.75 to 3.0 weight percent.
14. A glass fiber formed composition comprising:
64-75 weight percent SiO 2 ;
16-24 weight percent Al 2 O 3 ;
8-11 weight percent MgO;
0.25-3 weight percent Li 2 O; and
no more than 1.0 weight percent of CaO impurities, wherein said glass fibers produced from said composition have a fiberizing temperature of less than about 2650° F., a modulus of greater than 12 MPsi, and a strength of greater than about 700 KPsi.
15. The high strength glass fiber of claim 14 , wherein said fiber has a liquidus temperature that is at least 80° F. below the fiberizing temperature.
16. The high strength glass fiber of claim 14 , wherein said fiber has a fiberizing temperature less than about 2600° F.
17. The glass fiber of claim 16 , wherein said fiber has a liquidus temperature that is at least 80° F. below said fiberizing temperature.
18. The glass fiber of claim 14 , wherein said fiber has a pristine fiber tensile strength greater than about 730 KPsi.
19. The glass fiber of claim 14 , wherein said fiber has a ΔT of at least 80° F.
20. The glass fiber of claim 14 , wherein:
said Al 2 O 3 is present in said composition in an amount from about 17 to about 22 weight percent;
said MgO is present in said composition in an amount from about 9 to about 11 weight percent; and
said Li 2 O is present in said composition in an amount from about 1.75 to 3.0 weight percent.