Thermoplastic polycarbonate compositions
View Patent ↗Disclosed herein is a thermoplastic composition comprising: a polycarbonate; an impact modifier; a polycarbonate-polysiloxane copolymer; a poly(arylene ether)-polysiloxane copolymer; and an organophosphate in an amount of 2 to 20 weight percent based on the combined weight of polycarbonate, impact modifier, polycarbonate-polysiloxane copolymer, and poly(arylene ether)-polysiloxane copolymer, wherein the composition has a notched Izod impact strength of greater than or equal to 4 kilojoules per square meter (kJ/m 2 ) as determined according to ISO 180/A, a melt viscosity rate of less than or equal to 130 Pascal seconds (Pa·s) as determined according to ISO11443 at 1500 s −1 and 280° C., and a UL94 rating of V1 or better at 0.8 millimeter thickness.
1. A thermoplastic composition comprising:
30 to 85 weight percent of a polycarbonate, based on the total weight of the composition;
an impact modifier;
a polycarbonate-polysiloxane copolymer;
a poly(arylene ether)-polysiloxane copolymer;
an organophosphate in an amount of 2 to 20 weight percent based on the combined weight of polycarbonate, impact modifier, polycarbonate-polysiloxane copolymer and poly(arylene ether)-polysiloxane copolymer,
wherein the composition has a notched Izod impact strength of greater than or equal to 4 kilojoules per square meter (kJ/m2) as determined according to ISO 180/A, a melt viscosity rate of less than or equal to 130 Pascal seconds (Pa s) as determined according to ISO 11443 at 1500 s-1 and 280° C., and a UL 94 rating of V1 or better at 0.8 millimeter thickness.
2. The thermoplastic composition of claim 1 , wherein the composition has a notched Izod impact strength of greater than or equal to 6 kilojoules per square meter (kJ/m 2 ) as determined according to ISO 180/A.
3. The thermoplastic composition of claim 1 , wherein the composition has a notched Izod impact strength of greater than or equal to 10 kilojoules per square meter (kJ/m2) as determined according to ISO 180/A.
4. The thermoplastic composition of claim 1 , wherein the composition has a UL94 rating of V1 or better at 0.6 millimeters thickness.
5. The thermoplastic composition of claim 1 , wherein the composition has a heat deflection temperature of greater than or equal to 80° C. as determined by ISO 75/A.
6. The thermoplastic composition of claim 1 , wherein the impact modifier comprises methyl methacrylate-butadiene- styrene; acrylonitrile-butadiene-styrene, acrylonitrile-styrene-butyl acrylatemethyl, methacrylate-acrylonitrile-butadiene-styrene, acrylonitrile-ethylene-propylene-diene-styrene, or a combination of two or more of the foregoing.
7. The thermoplastic composition of claim 1 , wherein the composition comprises the impact modifier in an amount of 1 to 15 weight percent, based on the total weight of the composition.
8. The thermoplastic composition of claim 1 , wherein the composition comprises the polycarbonate-polysiloxane copolymer in an amount of 2 to 25 weight percent, based on the total weight of the composition.
9. The thermoplastic composition of claim 1 , wherein the poly(arylene ether)-polysiloxane block copolymer comprises polysiloxane in an amount of 5 to 50 weight percent, based on the total weight of the copolymer.
10. The thermoplastic composition of claim 1 , wherein the composition comprises the poly(arylene ether)-polysiloxane copolymer in an amount of 2 to 20 weight percent based on the total weight of the composition.
11. The thermoplastic composition of claim 1 , wherein the composition has a total siloxane content of 1 to 10 weight percent based on the total weight of the composition.
12. A thermoplastic composition comprising:
30 to 85 weight percent of a polycarbonate;
1 to 15 weight percent of an impact modifier;
2 to 25 weight percent of a polycarbonate-polysiloxane copolymer;
2 to 20 weight percent of a poly(arylene ether)-polysiloxane copolymer;
2 to 20 weight percent of an organophosphate, wherein weight percent is based on total weight of the composition,
wherein the composition has a notched Izod impact strength of greater than or equal to 4 kilojoules per square meter (kJ/m2) as determined according to ISO 180/ A, a melt viscosity rate of less than or equal to 130 Pascal seconds (Pa s) as determined according to IS011443 at 1500 s-1 and 280° C., and a UL 94 rating of V1 or better at 0.6 millimeter thickness.
13. A thermoplastic composition comprising:
30 to 85 weight percent of a bis-phenol A polycarbonate;
1 to 15 weight percent of a bulk polymerized acrylonitrile-butadiene-styrene copolymer;
2 to 25 weight percent of a polycarbonate-polysiloxane copolymer;
2 to 20 weight percent of a poly(arylene ether)-polysiloxane copolymer having a siloxane content of 25 to 35 weight percent based on the total weight of the copolymer;
2 to 20 weight percent of an organophosphate, wherein weight percent is based on total weight of the composition,
wherein the composition has a notched Izod impact strength of greater than or equal to 4 kilojoules per square meter (kJ/m2) as determined according to ISO 180/A, a melt viscosity rate of less than or equal to 130 Pascal seconds (Pa s) as determined according to IS011443 at 1500 s-1 and 280° C., and a UL94 rating of V1 or better at 0.6 millimeter thickness.