Use of gelatin and a cross-linking agent for producing cross-linking medical glues

1. A method of producing and applying a medical glue to an area of application of a human or animal body, the medical glue forming a cross-linked gelatin gel in the area of application of the human or animal body, the method comprising:

providing (A) a gelatin which has been partially cross-linked enzymatically by a transglutaminase and (B) a transglutaminase, both in separate chambers of a multi-chamber applicator; and

applying said partially cross-linked gelatin and the transglutaminase simultaneously or consecutively to the area of application, resulting in formation of the medical glue,

wherein said partially cross-linked gelatin and the transglutaminase are in the separate chambers until said partially-cross-linked gelatin and the transglutaminase are applied simultaneously or consecutively to the area of application, and wherein a 6.7% by weight (wt.) standard solution of said partially cross-linked gelatin in water at 60° C. has a viscosity of 7 mPa·s or more as a result of said partial cross-linking.

2. The method according to claim 1 , wherein the gelatin is a fish gelatin.

3. The method according to claim 1 , comprising providing said partially cross-linked gelatin in the form of an aqueous solution and providing the transglutaminase in a separate aqueous solution.

4. The method according to claim 3 , comprising simultaneously applying the aqueous solution comprising said partially cross-linked gelatin and the aqueous solution comprising the transglutaminase by injection using the multi-chamber applicator.

5. The method according to claim 1 , wherein providing said partially cross-linked gelatin and the transglutaminase in the separate chambers of a multi-chamber applicator comprises providing said partially cross-linked gelatin in the form of an aqueous solution and providing the transglutaminase in a solid form.

6. The method according to claim 1 , wherein the gelatin concentration in the medical glue amounts to 5 to 20% by wt.

7. The method according to claim 1 , wherein the cross-linked gelatin gel has a gel point that is reached 10 minutes or less after the start of a cross-linkage reaction, based on a predetermined temperature of the area of application.

8. The method according to claim 1 , wherein the cross-linked gelatin gel has a gel strength of 100 g or more, as measured with a plunger with a diameter of 12.7 mm at a penetration depth of 4 mm.

9. The method according to claim 1 , wherein the cross-linked gelatin gel has a gel strength and a gel point, wherein the gel strength of said cross-linked gelatin gel increases in the first 10 min after reaching the gel point at a rate of 5 to 200 mN/cm 2 min.

10. The method according to claim 1 , wherein the cross-linked gelatin gel has an adhesion on a smooth plastic surface of 200 mN/cm 2 or more.

11. The method according to claim 1 , wherein the medical glue comprises a viscosity-increasing polymer with a proportion of 1 to 10% by wt., based on the solid contents of the glue.

12. The method according to claim 11 , wherein the viscosity increasing polymer is carboxymethylcellulose.

13. The method according to claim 1 , wherein the medical glue comprises one or more therapeutic active substances.

14. The method according to claim 1 , wherein the area of application comprises human or animal skin that is injured and/or burned.

15. The method according to claim 1 , comprising fixing autologous or allogenic tissue in an area of application of the human or animal body, comprising applying the medical glue to the area of the tissue.

16. The method according to claim 1 , comprising fixing an implant in an area of application of the human or animal body, comprising applying the medical glue to the implant.