Solid phase polymerization catalyst system
View Patent ↗The invention is a method for making condensation polymers, such as polyethylene terephthalate polyester. The method includes introducing a catalyst system, which includes a coordination catalyst component and an acid component, to a polycondensation reaction.
1. A method for making polyethylene terephthalate resin, comprising:
polymerizing polyethylene terephthalate prepolymers via melt phase polycondensation to achieve polyethylene terephthalate polymers having an intrinsic viscosity of at least about 0.45 dL/g;
introducing a coordination catalyst;
introducing an acid having a pKa less than about 0 when the reaction melt has a carboxyl end group concentration of more than 50 microequivalents per gram; and
thereafter solid state polymerizing the polyethylene terephthalate polymers.
2. A method according to claim 1 , wherein the coordination catalyst includes one or more of titanium catalysts, germanium catalysts, antimony catalysts, or aluminum catalysts.
3. A method according to claim 1 , further comprising the step of introducing a supplemental catalyst in conjunction with the introduction of the coordination catalyst.
4. A method according to claim 3 , wherein the supplemental catalyst includes one or more of cobalt catalysts, manganese catalysts, or zinc catalysts.
5. A method according to claim 4 , wherein the coordination catalyst and the supplemental catalyst are introduced in amounts sufficient to promote melt phase polycondensation.
6. A method according to claim 1 , wherein the acid is introduced to the polyethylene terephthalate polymers after the completion of melt phase condensation polymerization and before initiating solid state polymerization.
7. A method according to claim 1 , wherein the acid is introduced to the polyethylene terephthalate polymers at an extruder.
8. A method according to claim 1 , wherein the acid has a pKa less than about −2.0.
9. A method according to claim 1 , wherein the acid is liquid at near ambient temperatures.
10. A method according to claim 1 , wherein the acid comprises one or more acids that are substantially free of a salt form.
11. A method according to claim 1 , wherein the solid state polymerization step achieves an improved rate of intrinsic viscosity lift (SSP IV lift) as compared with an otherwise comparable method that employs a catalyst system that is devoid of a strong acid component.
12. A method according to claim 1 , wherein the step of solid state polymerizing the polyethylene terephthalate polymers yields polyethylene terephthalate resin, and further comprising the step of forming the polyethylene terephthalate resin into a sheet, a film, a preform, a container, a bottle, a tray, a fiber, or other article.
13. A method for making polyethylene terephthalate resin, comprising:
polymerizing polyethylene terephthalate prepolymers via melt phase polycondensation in the presence of a catalyst system to achieve a polycondensation intermediate having an intrinsic viscosity of at least about 0.40 dL/g, the catalyst system comprising a coordination catalyst, a supplemental catalyst, and an acid having a pKa less than about 0; and
thereafter solid state polymerizing the polycondensation intermediate.
14. A method according to claim 13 , wherein the step of polymerizing polyethylene terephthalate prepolymers via melt phase polycondensation yields as the polycondensation intermediate polyethylene terephthalate polymers having an intrinsic viscosity of at least about 0.45 dL/g.
15. A method according to claim 13 , wherein the coordination catalyst includes one or more of titanium catalysts, germanium catalysts, antimony catalysts, or aluminum catalysts.
16. A method according to claim 13 , wherein the supplemental catalyst includes one or more of cobalt catalysts, manganese catalysts, or zinc catalysts.
17. A method according to claim 13 , wherein the acid has a pKa less than about −2.0.
18. A method according to claim 13 , wherein the solid state polymerization step achieves an improved rate of intrinsic viscosity lift (SSP IV lift) as compared with an otherwise comparable method that employs a catalyst system that is devoid of a strong acid component.
19. A method for making polyethylene terephthalate resin, comprising:
polymerizing polyethylene terephthalate prepolymers via melt phase polycondensation in the presence of a coordination catalyst to yield polyethylene terephthalate polymers;
thereafter introducing to the polyethylene terephthalate polymers an acid having a pKa less than about 0; and
solid state polymerizing the polyethylene terephthalate polymers.
20. A method according to claim 19 , wherein the step of polymerizing polyethylene terephthalate prepolymers comprises polymerizing polyethylene terephthalate prepolymers via melt phase polycondensation to yield polyethylene terephthalate polymers having an intrinsic viscosity of at least about 0.45 dL/g.
21. A method according to claim 19 , wherein the coordination catalyst includes one or more of titanium catalysts, germanium catalysts, antimony catalysts, or aluminum catalysts.
22. A method according to claim 19 , wherein the step of polymerizing polyethylene terephthalate prepolymers via melt phase polycondensation comprises polymerizing polyethylene terephthalate prepolymers in the presence of a coordination catalyst and a supplemental catalyst.
23. A method according to claim 22 , wherein the supplemental catalyst includes one or more of cobalt catalysts, manganese catalysts, or zinc catalysts.
24. A method according to claim 19 , wherein the acid is introduced to the polyethylene terephthalate polymers after the completion of melt phase condensation polymerization and before initiating solid state polymerization.
25. A method according to claim 19 , wherein the acid is introduced to the polyethylene terephthalate polymers at an extruder.
26. A method according to claim 19 , wherein the acid is liquid at near ambient temperatures.
27. A method according to claim 19 , wherein the acid has a pKa less than about −2.0.
28. A method according to claim 19 , wherein the acid comprises one or more acids that are substantially free of a salt form.
29. A method according to claim 19 , wherein the solid state polymerization step achieves an improved rate of intrinsic viscosity lift (SSP IV lift) as compared with an otherwise comparable method that employs a catalyst system that is devoid of a strong acid component.