Formation of thin uniform coatings on blade edges using isostatic press
View Patent ↗The invention discloses utilizing isostatic-press (IP) processes apply a polymeric material (e.g, a PTFE foil) to uncoated razor blade edges forming thin, dense, and uniform coatings on blade edges which in turn exhibit low initial cutting forces correlating with more comfortable shaves. The isostatic press may be a hot isostatic press (HIP) or a cold isostatic press (CIP) or any other isostatic press process. The HIP conditions may include an environment of elevated temperatures and pressures in an inert atmosphere. The CIP conditions may include room temperature and elevated pressure. The polymeric material may be a fluoropolymer or non-fluoropolymeric material or any composite thereof. The lower surface of the polymeric material may be modified (e.g., chemical etching) to enhance adhesion to the blade edge. Two or more layers of polymeric material of similar or different properties may be isostatically pressed onto the uncoated blades.
1. A method for forming a razor blade edge comprising: initially applying, by isostatic press (IP), at least one polymeric material having an upper surface and a lower surface to at least one blade edge to form an isostatically-pressed coating on said at least one blade edge, wherein said isostatically-pressed coating ranges in thickness from about 10 nm to about 100 nm and wherein said razor blade is comprised of steel, Chromium (Cr), Diamond-like Carbon (DLC), Amorphous Diamond, or Chromium/Platinum (Cr/Pt).
2. The method of claim 1 wherein said isostatic pressing is comprised of a hot isostatic press (HIP) or a cold isostatic press (CIP).
3. The method of claim 2 wherein said HIP further comprises a temperature in the range of about 300° C. to about 380° C. and an inert atmosphere of argon or nitrogen.
4. The method of claim 2 wherein said HIP further comprises a pressure range of about 100 MPa to about 550 MPa.
5. The method of claim 2 wherein said HIP is applied for a time ranging from about 10 minutes to about 10 hours.
6. The method of claim 1 wherein said at least one blade edge is initially uncoated.
7. The method of claim 1 wherein said lower surface of said polymeric material is modified.
8. The method of claim 1 wherein said polymeric material comprises a fluoropolymeric material.
9. The method of claim 1 wherein said at least one polymeric material has an average molecular weight in the range of about 10,000 Dalton to about 1,000,000 Dalton.
10. The method of claim 1 wherein said isostatically-pressed coating is substantially uniform in thickness.
11. The method of claim 1 wherein said isostatically-pressed coating has a substantially uniform surface morphology.
12. The method of claim 1 wherein said isostatically-pressed coating has substantially zero porosity.
13. The method of claim 1 wherein said polymer comprises a non-fluoropolymeric material.