Lithium ion secondary battery
View Patent ↗A lithium ion secondary battery is capable of improving the energy density and power density and excellent in high rate cycle characteristics applicable to hybrid cars, etc. The lithium ion secondary battery including a positive electrode of a lithium transition metal complex oxide, a negative electrode for absorbing/releasing lithium, and a non-aqueous electrolyte containing a lithium salt, in which the negative electrode has a negative electrode active material using a non-graphitizing carbon (spacing d(002) of 0.360 nm or more by XRD) and a graphitizing carbon (spacing d(002) of 0.339 nm or more and less than 0.360 nm by XRD) surface-modified at a thickness in a range from 10 nm to 100 nm in admixture, comprising the non-graphitizing carbon and the graphitizing carbon at a ratio in the range of 90 to 50 wt % :10 to 50 wt % and, further, graphitizing carbon having a grain size larger than that of the non-graphitizing carbon is used.
1. A lithium ion secondary battery comprising a positive electrode of absorbing/releasing lithium, a negative electrode of absorbing/releasing lithium and an electrolyte, wherein
the negative electrode has a negative electrode active material,
the negative electrode active material contains a non-graphitizing carbon and a graphitizing carbon which is coated on the surface with the non-graphitizing carbon,
the non-graphitizing carbon is in the range from 90 to 50 wt % and the graphitizing carbon is in the range from 10 to 50 wt % based on the total weight of the non-graphitizing carbon and the graphitizing carbon, with the total of them being 100%, and
the average grain size of the graphitizing carbon is larger than the average grain size of the non-graphitizing carbon.
2. A lithium ion secondary battery according to claim 1 , wherein the graphitizing carbon has a layer containing the non-graphitizing carbon on the surface.
3. A lithium ion secondary battery comprising a positive electrode of absorbing/releasing lithium, a negative electrode of absorbing/releasing lithium and an electrolyte, wherein
the negative electrode has a negative electrode active material,
the negative electrode active material contains a non-graphitizing carbon and a graphitizing carbon which is coated on the surface with the non-graphitizing carbon,
the non-graphitizing carbon is in the range from 90 to 50 wt % and the graphitizing carbon is in the range from 10 to 50 wt % based on the total weight of the non-graphitizing carbon and the graphitizing carbon, with the total of them being 100%,
the graphitizing carbon has a layer containing the non-graphitizing carbon on the surface, the thickness of the layer being from 10 nm to 100 nm.
4. A lithium ion secondary battery according to claim 3 , wherein the average grain size of the graphitizing carbon is larger than the average grain size of the non-graphitizing carbon.
5. A lithium ion secondary battery comprising a positive electrode of absorbing/releasing lithium, a negative electrode of absorbing/releasing lithium and an electrolyte, wherein
the negative electrode has a negative electrode active material,
the negative electrode active material contains a non-graphitizing carbon and a graphitizing carbon which is coated on the surface with the non-graphitizing carbon,
the non-graphitizing carbon is in the range from 90 to 50 wt % and the graphitizing carbon is in the range from 10 to 50 wt % based on the total weight of the non-graphitizing carbon and the graphitizing carbon, with the total of them being 100%, and
the spacing d(002) of the non-graphitizing carbon is 0.360 nm or more and the spacing d (002) of the graphitizing carbon is 0.339 nm or more and less than 0.360 nm.
6. A lithium ion secondary battery according to claim 5 , wherein the average grain size of the graphitizing carbon is larger than the average grain size of the non-graphitizing carbon.
7. A lithium ion secondary battery according to claim 5 , wherein the graphitizing carbon has a layer containing the non-graphitizing carbon on the surface.
8. A lithium ion secondary battery according to claim 7 , wherein the thickness of the layer is from 10 nm to 100 nm.