Casing layer for polyurethane-covered and polyurea-covered golf balls
View Patent ↗This invention is related to multi-layer golf balls having at least one layer containing a neutralized high acid ionomer linked to a grafted metallocene copolymer, where the golf balls exhibit improved performance characteristics and properties.
1. A golf ball comprising:
a core;
a casing layer disposed about the core, wherein the casing layer comprises a blend comprising:
a high acid ionomer comprising greater than about 16 percent acid groups by weight of the high acid ionomer, wherein between about 25 percent and about 70 percent of the acid groups are neutralized with a metal cation,
a metallocene catalyzed polymer comprising at least one grafted moiety; and
an unneutralized acid copolymer comprising about 17 percent to about 30 percent acid groups by weight of the unneutralized acid copolymer; and
a cover having a hardness of about 30 to about 55 Shore D and comprising a composition formed from a polyurethane prepolymer and a hydroxy-terminated curing agent, wherein the polyurethane prepolymer comprises the reaction product of an isocyanate and a hydroxy-terminated component.
2. The golf ball of claim 1 , wherein the at least one grafted moiety is selected from the group consisting of maleic anhydride, fumaric anhydride or itaconic anhydride.
3. The golf ball of claim 1 , wherein the high acid ionomer is present in the blend in an amount of about 84 pph to about 67 pph based on the total blend.
4. The golf ball of claim 3 , wherein the blend comprises about 10 to about 40 pph of the metallocene catalyzed polymer based on the total blend.
5. The golf ball of claim 4 , wherein the blend comprises between about 2 and 4 pph of the unneutralized acid copolymer based on the total blend.
6. The golf ball of claim 1 , wherein between about 30 and 60 percent of the acid groups are neutralized in the high acid ionomer.
7. The golf ball of claim 1 , wherein the core comprises polybutadiene.
8. The golf ball of claim 1 , wherein the metallocene catalyzed polymer comprises a copolymer of ethylene and butene.
9. The golf ball of claim 8 , wherein the metallocene catalyzed polymer comprises maleic anhydride grafted metallocene catalyzed polymer.
10. The golf ball of claim 1 , wherein the unneutralized acid copolymer has a melt flow index of 60.
11. A golf ball comprising:
a core;
a casing layer disposed about the core, wherein the casing layer comprises a blend comprising:
a high acid ionomer comprising greater than about 16 percent acid groups by weight of the high acid ionomer, wherein between about 25 percent and about 70 percent of the acid groups are neutralized with a metal cation; and
a metallocene catalyzed polymer comprising at least one grafted moiety; and
an unneutralized acid copolymer comprising greater than 16 percent acid groups by weight of the unneutralized acid copolymer;
a cover comprising a composition formed from a polyurethane prepolymer and a hydroxy-terminated curing agent, wherein the polyurethane prepolymer comprises the reaction product of an isocyanate and a hydroxy-terminated component.
12. The golf ball of claim 10 , wherein the unneutralized acid copolymer is present in the blend in an amount between about 2 and 4 pph based on the total blend.
13. The golf ball of claim 10 , wherein between about 30 percent and about 60 percent of the acid groups in the high acid ionomer are neutralized.
14. The golf ball of claim 10 , wherein the at least one grafted moiety comprises maleic anhydride.
15. The golf ball of claim 10 , wherein the core comprises polybutadiene.
16. The golf ball of claim 10 , wherein the high acid ionomer is present in the blend in an amount ranging from about 84 to about 67 pph based on the total blend.
17. The golf ball of claim 16 , wherein the metallocene catalyzed polymer is present in the blend in an amount ranging from about 16 to about 33 pph based on the total blend.
18. The golf ball of claim 11 , wherein the unneutralized acid copolymer has a melt flow index of 60.
19. A golf ball comprising:
a core;
a casing layer disposed about the core, wherein the casing layer comprises a blend comprising:
a high acid ionomer comprising between about 17 and 25 percent acid groups by weight of the high acid ionomer, wherein between about 30 percent and about 60 percent of the acid groups are neutralized with a metal cation; and
a metallocene catalyzed polymer having the following general formula:
wherein R 7 comprises a hydrogen, a linear or branched alkyl group, an aromatic or heterocyclic group, or a combination thereof; R 8 , R 9 , R 11 , and R 12 comprises a hydrogen, a lower alkyl group comprising 1 to 5 carbon atoms, a carbocyclic group, an aromatic or heterocyclic group, or a combination thereof; and x, y, and z are the relative percentages of each co-monomer, wherein x ranges from 1 percent to 99 percent, y ranges from 99 percent to 1 percent, and z ranges from 0 percent to 49 percent; and
an unneutralized acid copolymer comprising greater than 16 percent acid groups by weight of the melt flow modifier;
a cover comprising a composition formed from a polyurethane prepolymer and a hydroxy-terminated curing agent, wherein the polyurethane prepolymer comprises the reaction product of an isocyanate and a hydroxy-terminated component.
20. The golf ball of claim 19 , wherein the unneutralized acid copolymer has a melt flow index of 60.