Method and reagent for producing narrow, homogenous reagent strips
View Patent ↗The present invention concerns a reagent coating mass which can be used in slot-die-coating of flat support materials in the manufacturing processes of test strips. Advantageously, the reagent mass of the invention exhibits certain superior rheological properties such as viscosity, surface tension and thixotropy. The reagent mass is preferably used to coat thin, narrow and homogeneous stripes of reagent material onto flat web material.
1. A process for producing a reagent layer on a solid support material, comprising the steps of:
providing a solid support material;
moving said solid support material relative to a slot-die-coating head;
maintaining a defined distance between the surface of said solid support material and said slot-die-coating head;
depositing a shear thinning, at least slightly thixotropic reagent through said slot-die-coating head to create a continuous stripe of reagent on said solid support material, wherein said reagent has a viscosity of between about 95 to 115 mPa-s and a surface tension of between about 33 and 42 mN/m; and
drying the coated reagent stripe on said support material.
2. The process according to claim 1 , wherein said reagent is deposited on said solid support at a coating flux rate of about 5.5 to about 30 g/min.
3. The process according to claim 1 , wherein said reagent is deposited on said solid support at a coating flux rate of about 13 to about 15 g/min.
4. The process according to claim 1 , wherein said defined distance between said slot-die-coating head and said support material is between 30 and 90 μm.
5. The process according to claim 1 , wherein said support material moves relative to said slot-die-coating head at a rate of between 20 and 80 m/min.
6. The process according to claim 1 , wherein said support material moves relative to said slot-die-coating head at a rate of between 30 and 40 m/min.
7. The process according to claim 1 , wherein said stripe of reagent is less than 1 cm wide.
8. The process according to claim 1 , wherein after drying, said reagent on said solid support material has a height of less than 10 μm.
9. The process according to claim 1 , said reagent including at least one of buffers, enzymes, mediators, stabilizers, thickeners, proteins, indicators, dyes, film formers, surfactants and co-factors.
10. The process according to claim 9 , said reagent further including at least one of silica, xanthan gum and CMC.
11. The process according to claim 9 , said reagent further including silica and at least one of xanthan gum and CMC.
12. The process according to claim 9 , said reagent further including silica, xanthan gum and CMC.
13. In a process for preparing biosensors from a webbing of a substrate, the improvement comprising:
depositing a continuous stripe of reagent onto the webbing in the form of a shear thinning, at least slightly thixotropic reagent having a viscosity of between about 95 to 115 mPa-s and a surface tension of between about 33 and 42 mN/m; and
drying the coated reagent stripe on said support material.
14. A process for preparing biosensors comprising:
depositing a continuous stripe of reagent onto a webbing in the form of a shear thinning, at least slightly thixotropic reagent having a viscosity of between about 95 to 115 mPa-s and a surface tension of between about 33 and 42 mN/m;
applying a spacer layer over the reagent; and
attaching the spacer layer to the webbing.