Self-deposited coatings on magnesium alloys
View Patent ↗Some articles such as automobile components that have been constructed from steel and/or aluminum alloy parts are now being fitted with magnesium parts whose surfaces may need to be protected against corrosion. To do this an e-coating pre-film may be formed on the part's magnesium surfaces by exposing it to a conventional e-coating emulsion. And there is no need to supply a current or potential to the part or component. Magnesium's high reactivity with acidic or neutral aqueous mediums is itself a sufficient driving force to facilitate the deposition of an e-coating pre-film. At the same time any steel or aluminum alloy parts will remain unaffected. The article with a protective e-coating pre-film formed solely on its magnesium surfaces may now be advanced through a paint-line that includes conventional processes aimed at treating the component's steel and aluminum alloy parts. The process may be practiced where the magnesium surface comprises a magnesium-containing conversion or anodized coating.
1. A method for protecting an article against corrosion, the article comprising a magnesium surface portion and at least one of a steel surface portion and aluminum surface portion, the method comprising:
providing a first aqueous e-coating emulsion in which water can react with the magnesium surface to generate hydroxyl ions at the interface of the magnesium surface and the e-coating emulsion, the emulsion having dispersed therein a cathodic electrocoat composition that destabilizes in a basic aqueous environment; and
exposing at least the magnesium surface of the article to the first aqueous e-coating emulsion without applying a current or potential to the article to deposit an e-coating pre-film exclusively on the magnesium surface, and wherein the e-coating pre-film provides the magnesium surface with temporary protection against a chemical reaction with water in a neutral or acidic aqueous medium;
exposing at least the steel and/or aluminum surfaces of the article to a conversion coating solution to deposit a conversion coating on the steel and/or aluminum surface portions; and
exposing at least the steel and/or aluminum surface portions to a second aqueous e-coating emulsion and applying a current or potential to the article such that it serves as a cathode, and wherein the application of a current or potential deposits an e-coating pre-film on the aluminum and/or steel surface portions.
2. The method of claim 1 , wherein the article is an automobile body structure.
3. The method of claim 1 , wherein the magnesium surface portion of the article is an automotive body panel.
4. The method of claim 1 in which a magnesium surface portion of the article comprises a magnesium-containing conversion coating.
5. The method of claim 1 wherein providing a first aqueous e-coating emulsion comprises providing an e-coating emulsion having dispersed therein a cathodic electrocoat that comprises an aminoepoxy resin neutralized with a weak organic acid and emulsified in water.
6. The method of claim 1 , wherein providing a first aqueous e-coating emulsion comprises providing an e-coating emulsion having dispersed therein a cathodic electrocoat that destabilizes in a basic environment that has a pH value of about 10.5 or greater.
7. The method of claim 1 , wherein providing a first aqueous e-coating emulsion comprises providing an e-coating emulsion that comprises a pH of about 5.8 to about 6.2, a conductivity of about 1300 to about 2000 microsiemens/cm, and about 15 to about 35 acid milliequivalents per gram of nonvolatile matter.
8. The method of claim 1 , wherein exposing at least the steel and/or aluminum surface portions to a second aqueous e-coating emulsion comprises exposing the surfaces to an e-coating emulsion that is the same composition as the first e-coating emulsion.
9. The method of claim 1 , wherein exposing at least the magnesium surface of the automobile component to the first e-coating emulsion comprises immersing the automobile component in a bath of the first e-coating emulsion.
10. The method of claim 1 , wherein exposing at least the magnesium surface of the article to the first e-coating emulsion comprises painting at least the magnesium surface portion with the first e-coating emulsion using a painting tool.
11. The method of claim 1 , wherein exposing at least the magnesium surface of the article to the first e-coating emulsion comprises spraying at least the magnesium surface with the first e-coating emulsion.